Sintering Properties and Optimal Blending Schemes of Iron Ores

被引:1
作者
Dauter Oliveira
机构
[1] School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing
[2] VALE Shanghai Office
关键词
sintering; iron ore; sintering property indices; ore blending scheme;
D O I
10.13228/j.boyuan.issn1006-706x.2012.06.010
中图分类号
TF046.4 [];
学科分类号
080601 ;
摘要
In order to obtain good sintering performance,it is important to understand sintering properties of iron ores.Sintering properties including chemical composition,granulation and high-temperature behaviors of ores from China,Brazil and Australia.Furthermore,several indices were defined to evaluate sintering properties of iron ores.The results show that:for chemical composition,Brazilian ores present high TFe,low SiO2,and low Al2O3 content.For granulation,particle diameter ratio of Brazilian ores are high;particle intermediate fraction of Chinese concentrates are low;and average particle size and clay type index of Australian ores are high.For high-temperature properties,ores from China,Brazil and Australia present different characteristics.Ores from different origins should be mixed together to obtain good high-temperature properties.According to the analysis of each ore’s sintering properties,an ore blending scheme(Chinese concentrates 20%+Brazilian ores 40%+Australian ores 40%) was suggested.Moreover,sinter pot test using blending mix was performed,and the results indicated that the ore blending scheme led to good sintering performance and sinter quality.
引用
收藏
页码:1 / 5
页数:5
相关论文
共 4 条
[1]   基于铁矿粉高温特性互补的烧结优化配矿 [J].
吴胜利 ;
戴宇明 ;
Dauter Oliveira ;
裴元东 ;
徐健 ;
韩宏亮 .
北京科技大学学报, 2010, 32 (06) :719-724
[2]   强化制粒对高铁低硅混合料烧结的影响 [J].
朱德庆 ;
张克诚 ;
何奥平 ;
范晓慧 ;
曾新中 ;
肖力华 .
烧结球团, 2003, (01) :9-13
[3]   Al2O3/SiO2对低温烧结成矿规律的影响 [J].
刘晓荣 ;
邱冠周 ;
蔡汝卓 ;
林淑芳 .
钢铁, 2001, (03) :5-8
[4]  
Effect of Al2O3 and MgO Additions on Liquidus for the CaO-SiO2-FeOx System at 1573 K .2 Kimura H,Ogawa T,Kakki M,et al. ISIJ International . 2005