Luminescence Properties of Green-Emitting Phosphor (Ba1-x,Srx2SiO4∶Eu2+ for White LEDS

被引：13
作者：
刘红利
何大伟
沈芳
机构：
[1] Ministry of Education Key Laboratory Laboratory of Materials for Information Storage and Display Institute of Photoelectron Technology Beijing Jiaotong University Beijing 100044 China
[2] Ministry of Education Key Laboratory Laboratory of Materials for Information Storage and Display Institute of Photoelectron Technology Beijing Jiaotong University Beijing 100044 China
来源：
JournalofRareEarths | 2006年 / 01期
关键词：
phosphor silicate; luminescence; rare earths;
D O I：
暂无
中图分类号：
O482.31 [发光学];
学科分类号：
070205 ; 0805 ; 080502 ; 0809 ;
摘要：
The （Ba 1-xSrx）2SiO4∶Eu 2+ green-emitting phosphors were synthesized by conventional solid-state reaction in a CO-reductive atmosphere, and their luminescent properties were investigated. The XRD data show that the Ba/Sr ratio not only affects the lattice parameters, but also influences the emission peak. The excitation spectra indicate that this phosphor can be effectively excited by UV light from 370 to 470 nm. The emission band is due to the 4f65d1→4f7 transition of the Eu 2+ ion. With an increase in x, the emission band shifts to longer wavelength and the reason was discussed. The emission spectra exhibit a satisfactory green performance under different excitation wavelength（380, 398, 412, 420, 460 nm）. （Ba 1-xSrx）2SiO4∶Eu 2+ is a promising phosphor for green white-lighting-emission diode by ultraviolet chip.
引用
收藏
页码：121 / 124 +134
页数：5
相关论文
共 6 条
  • [1] Rareearthphosphors:fundamentalsandapplications. RondaC.R,K櫣stelT,NikolH. J.AlloysandCom pounds . 1998
  • [2] Red deficiency compensatingphosphor. LoweryCH,MuellerG,MuellerR. USPatent6351069B1 . 2002
  • [3] Phosphorfreehigh luminous efficiencywhitelight emittingdiodescomposed ofInGaNmulti quantumwell. YamadaM,NarukawaY,MukaiT. Japanese Journal of Applied Physics . 2002
  • [4] Thebetatoorfrom alphatransitioninSr sub2SiO sub4(andCa sub2SiO sub4,K sub2SeO sub4etc.),involvingamodu latedstructure. HydeBG,SellarJR,StenbergL. Acta Crystallographica . 1986
  • [5] Energytrans ferandphotoluminescenceofBaMgAl10O17co dopedwith Eu2+andMn2+. YangPing,YaoGuangqing,LinJianhua. OpticalMaterials . 2004
  • [6] Luminescencepropertiesof2(Sr1-xMxO)·(1-y)P2O5·yB2O3∶Eu2+underUVexci tation. LiuChuntang,HeDawei. JournalofRareEarths . 2003
1