Impact Toughness of an NM400 Wear-Resistant Steel

被引：0

作者：

SONG Hongyu ^{[1
]}

LI Canming ^{[1
,2
]}

LAN Liangyun ^{[1
]}

ZHAO Dewen ^{[1
]}

WANG Guodong ^{[1
]}

机构：

[1] State Key Laboratory of Rolling and Automation,Northeastern University

[2] Laiwu Iron and Steel Group Co,Ltd

来源：

JournalofIronandSteelResearch(International) | 2013年 / 20卷 / 08期

关键词：

impact toughness; direct quenching; tempering; lower bainite; martensite packet;

D O I：

10.13228/j.boyuan.issn1006-706x.2013.08.009

中图分类号：

TG142.72 [耐磨钢];

学科分类号：

080502 ;

摘要：

An NM400 wear-resistant steel was hot rolled and then the plates were heat-treated by direct quenching and tempering (DQT) and reheat quenching and tempering (RQT) techniques,respectively.The Charpy impact test was carried out with an instrumented Charpy impact tester.The microstructure and fracture surface were investigated by a combination of optical microscopy,transmission electron microscopy and scanning electron microscopy methods.It was found that the impact toughness of DQT specimen was much higher than that of RQT specimen.The microstructure of both DQT and RQT specimens was characterized by a mixture of tempered lath martensite and lower bainite.The lower bainite in DQT specimen extended into prior austenite grains and the content was higher than that in RQT specimen.The lower bainite in DQT specimen improved the impact toughness by increasing the proportion of large-angle boundaries and relieving the stress concentration at the crack tip.A number of fine and dispersed carbides in DQT specimen also contributed to the improvement of the impact toughness.

引用

页码：72 / 77

页数：6

共 11 条

[1] Effect of direct quenching on microstructure and mechanical properties of medium-carbon Nb-bearing steel [J].

Yingli ZHAO Jie SHI Wenquan CAO Maoqiu WANG Gang XIE School of Material and Metallurgy Engineering Kunming University of Science and Technology Kunming China Institute for Structural Materials Central Iron and Steel Research Institute Beijing China .

Journal of Zhejiang University-Science A(Applied Physics & Engineering), 2010, 11 (10) :776-781

[2] X80管线钢的冲击断裂行为 [J].

邓伟 ;

高秀华 ;

秦小梅 ;

赵德文 ;

杜林秀 ;

王国栋 .

金属学报 , 2010, (05) :533-540

[3] 马氏体贝氏体复合组织的强度与韧性 [J].

宋余九 ;

芦锦堂 ;

刘静华 ;

沈莲 ;

饶启昌 ;

周惠久 .

金属热处理学报, 1982, (01) :11-27

[4]

Effect of Microstructures on Elevated-Temperature Wear Resistance of a Hot Working Die Steel [J] . Min-xian WEI,Shu-qi WANG,Lan WANG,Kang-min CHEN.&nbsp&nbspJournal of Iron and Steel Research International . 2011 (10)

[5]

Microstructural characteristics and toughness of the simulated coarse grained heat affected zone of high strength low carbon bainitic steel [J] . Liangyun Lan,Chunlin Qiu,Dewen Zhao,Xiuhua Gao,Linxiu Du.&nbsp&nbspMaterials Science & Engineering A . 2011

[6]

An investigation on the microstructure and mechanical properties of direct-quenched and tempered AISI 4140 steel [J] . A.H. Meysami,R. Ghasemzadeh,S.H. Seyedein,M.R. Aboutalebi.&nbsp&nbspMaterials and Design . 2009 (3)

[7]

Microstructure, mechanical properties and high stress abrasive wear behavior of air-cooled MnCrB cast steels [J] . Kaishuang Luo,Bingzhe Bai.&nbsp&nbspMaterials and Design . 2009 (5)

[8]

Study and Application of Heat Treatment of Multi-Element Wear-Resistant Low-Alloy Steel [J] . Zhi-qiang JIANG,Jian-ming DU,Xi-lan FENG.&nbsp&nbspJournal of Iron and Steel Research International . 2006 (1)

[9] On coherent transformations in steel [J].

Guo, Z ;

Lee, CS ;

Morris, JW .

ACTA MATERIALIA, 2004, 52 (19) :5511-5518

[10] The morphology and crystallography of lath martensite in Fe-C alloys [J].

Morito, S ;

Tanaka, H ;

Konishi, R ;

Furuhara, T ;

Maki, T .

ACTA MATERIALIA, 2003, 51 (06) :1789-1799

← 1 2 →