Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steelin Pure Water

被引：0

作者：

XingChen Liu ^{[1
,2
]}

HongLiang Ming ^{[1
]}

ZhiMing Zhang ^{[1
]}

JianQiu Wang ^{[1
]}

LiChen Tang ^{[3
]}

Hao Qian ^{[3
]}

YongCheng Xie ^{[3
]}

EnHou Han ^{[1
]}

机构：

[1] CAS Key Laboratory of Nuclear Materials and Safety Assessment,Institute of Metal Research,Chinese Academy of Sciences

[2] School of Materials Science and Engineering,University of Science and Technology of China

[3] Shanghai Nuclear Engineering Research and Design Institute LtdCo

来源：

Acta Metallurgica Sinica(English Letters) | 2019年 / 32卷 / 12期

关键词：

Alloy; 690TT; 405; SS; Fretting corrosion; Temperature;

D O I：

暂无

中图分类号：

TM623 [核电厂（核电站）];

学科分类号：

080802 ;

摘要：

In pressurized water reactor,fretting corrosion has become the main reason for the failure of 690 TT heat exchanger tubes.The effect of temperature on the fretting corrosion behavior between 690 TT tube and 405 stainless steel(SS) bar has been studied during 106 fretting cycles.The overall average coefficient of friction(COF) values descends with an increase in test temperature,while the width of worn scar becomes wider.The severest fretting corrosion happens when the test temperature is at 100℃.The wear mechanism differs at different test temperatures,from adhesive wear at room temperature to abrasive wear and delamination at 100℃,to abrasive wear at 200℃.Deformation slips,high residual strain concentration,and micro-cracks are found which are disadvantageous for the further service performance of the tubes.