DIFFUSION BONDING OF TiAl TO Ti AND TC4 ALLOY

被引：1
|
作者：
P. He
J. H. Zhang
J. C. Feng and Y. Y. Qian (National Key Laboratory of Advanced Welding Production Technology
机构：
来源：
ActaMetallurgicaSinica(EnglishLetters) | 2000年 / 01期
关键词：
diffusion bonding; interface reacting; TiAl;
D O I：
暂无
中图分类号：
TG146.2 [轻有色金属及其合金];
学科分类号：
080502 ;
摘要：
TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase arised closest to Ti base at 1173K and 1573K respectively. The phase structure of TiAl/ and the phase structure of TiAlwere observed be- tween AiAl and TC4 under respetive bonding temperature.The fiacture at tensile testing occurred in the bond - line, producing very flat fracture surfaces with some pull-out of the TiAl materials.The ultimate tensile strengths of the joint were approximate to γ-TiAl base marterial.
引用
收藏
页码：162 / 167
页数：6
相关论文
共 50 条
  • [21] TiAl diffusion bonding using Ni/Ti multilayers
    Simoes, Sonia
    Sofia Ramos, A.
    Viana, Filomena
    Teresa Vieira, M.
    Vieira, Manuel F.
    WELDING IN THE WORLD, 2017, 61 (06) : 1267 - 1273
  • [22] TiAl diffusion bonding using Ni/Ti multilayers
    Sónia Simões
    A. Sofia Ramos
    Filomena Viana
    M. Teresa Vieira
    Manuel F. Vieira
    Welding in the World, 2017, 61 : 1267 - 1273
  • [23] Diffusion bonding of laser surface modified TiAl alloy/Ni alloy
    Li, ZF
    Wu, GQ
    Huang, Z
    Ruan, Z
    MATERIALS LETTERS, 2004, 58 (27-28) : 3470 - 3473
  • [24] Diffusion in the interface region of Ti/TiAl-Nb bonding
    Kommel, Lembit
    DIFFUSION IN SOLIDS - PAST, PRESENT AND FUTURE, 2006, 249 : 193 - 200
  • [25] Vibration fatigue properties and deterioration mechanism of diffusion bonded TC4 titanium alloy
    Lei, Yi-wen
    Ma, Guang-lu
    Liu, Yue
    Zhao, Wei
    Wu, Hui -ping
    Li, Xi-feng
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2024, 34 (02) : 533 - 546
  • [26] Development of unified constitutive model for hot deformation behavior of TC4 with and without diffusion bonding
    Cai, Zhongman
    Chen, Haosheng
    Li, Can
    Chen, Jiarui
    Li, Xiaoxing
    Li, Yong
    20TH METAL FORMING INTERNATIONAL CONFERENCE, METAL FORMING 2024, 2024, 44 : 548 - 557
  • [27] Microstructure and Mechanical Properties of Vacuum Diffusion Bonded Ti2AlNb/Ti/TC4 Joint
    Wang, Yifeng
    Hu, Bingxu
    Wei, Yan
    Feng, Guangjie
    Deng, Dean
    CRYSTALS, 2021, 11 (07)
  • [28] DIFFUSION BONDING OF INTERMETALLIC COMPOUND TIAL
    NAKAO, Y
    SHINOZAKI, K
    HAMADA, M
    ISIJ INTERNATIONAL, 1991, 31 (10) : 1260 - 1266
  • [29] Interface evolution mechanism and mechanical properties of Ti311/TC4 laminated composites during hot-pressing diffusion bonding
    Yuan, Jingjiu
    Fan, Qunbo
    Liu, Weifeng
    Xu, Shun
    Yang, Lin
    Cheng, Xingwang
    Zhang, Hongmei
    Yan, Qianyun
    Wang, Le
    Zhang, Junjie
    MATERIALS CHARACTERIZATION, 2024, 211
  • [30] Diffusion Bonding of Dissimilar Intermetallic Alloys Based on Ti2AlNb and TiAl
    Zou, Jianying
    Cui, Yuyou
    Yang, Rui
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2009, 25 (06) : 819 - 824
12345