Effect of ultrasonic stirring on temperature distribution and grain refinement in Al-1.65%Si alloy melt

被引:0
作者
李军文 [1 ]
T Momono [2 ]
付莹 [1 ]
贾征 [1 ]
Y Tayu [3 ]
机构
[1] College of Material and Chemical Engineering, Liaoning University of Technology
[2] Faculty of Materials Science and Engineering, Muro ran Institute of Technology
[3] Faculty of Materials Science and Engineering, Muroran Institute of Technology
关键词
ultrasonic stirring; temperature distribution; ingot; grain refinement;
D O I
暂无
中图分类号
TG146.21 [];
学科分类号
080502 ;
摘要
A series of experiments were conducted for Al-1.65%Si (mass fraction) alloy melt to study the formation of grain refining structure with ultrasonic stirring. The cooling curves of ingots with ultrasonic were measured and compared with those without ultrasonic. At the same time, the effect of the time of ultrasonic stirring on solidification structure of ingots was investigated. The influence of ultrasonic on the grain-refining efficiency of ingots was analyzed. In order to well understand the melts behavior under ultrasonic, by using ammonium chloride solution, the simulation experiment was carried out and the temperature distribution in ingot with or without ultrasonic was compared. The results indicate that the ultrasonic reduces the temperature inhomogeneity of melt, i.e. the ultrasonic helps to homogenize the melt temperature. The effect of stirring and heat generation in ingot start to occur with increasing the time of ultrasonic stirring.
引用
收藏
页码:691 / 697
页数:7
相关论文
共 5 条
[1]   侧部导入超声处理对共晶Al-Si合金凝固特性的影响 [J].
刘清梅 ;
龚永勇 ;
侯旭 ;
戚飞鹏 ;
翟启杰 .
中国有色金属学报, 2007, (02) :308-312
[2]  
Effect of Ultrasonic Output Power on Refining the Crystal Structures of Ingots and Its Experimental Simulation[J]. Tadashi MOMONO.Journal of Materials Science & Technology. 2005(01)
[3]  
Effect of side transmission of power ultrasonic on structure of AZ81 magnesium alloy[J]. 张海波,翟启杰,戚飞鹏,龚永勇.Transactions of Nonferrous Metals Society of China. 2004(02)
[4]  
Effect Of Distribution Coefficient K<sub>0</sub> On The Structure Of Ultrasonic Ingots During Solidification Of Aluminium Alloys[J] . Li,Momono.Materials Technology . 2005 (4)
[5]   Regularities of the intensifying effect of ultrasonic treatment on titanium alloy pickling [J].
Eskin, GI ;
Sinyavskii, VS ;
Usova, VV .
PROTECTION OF METALS, 2003, 39 (06) :551-559