Influence of heat treatment on microstructure and mechanical properties of Mg-10Gd-3Y-1.2Zn-0.4Zr alloy

被引：9

作者：

李德江 ^{[1
]}

曾小勤 ^{[1
,2
]}

董杰 ^{[1
]}

翟春泉 ^{[1
]}

机构：

[1] National Engineering Research Center of Light Alloy Net Forming,Shanghai Jiao Tong University

[2] State Key Laboratory of Metal Matrix Composites,Shanghai Jiao Tong University

来源：

Transactions of Nonferrous Metals Society of China | 2008年 / 18(S1)卷 / S1期

关键词：

Mg-Gd-Y-Zn-Zr alloy; microstructure; LPSO structured phase; mechanical properties;

D O I：

暂无

中图分类号：

TG146.22 [];

学科分类号：

080502 ;

摘要：

Microstructure evolution and mechanical properties of the cast Mg-10Gd-3Y-1.2Zn-0.4Zr(mass fraction,%) alloy during annealing at 798 K for different time were investigated.In the as-cast state,the microstructure consists ofα-Mg,Mg5(Gd,Y,Zn) eutectic compounds and stacking faults(SF) of basal plane distributed from grain boundary to inner grain.During heat treatment at 798 K,the SF and parts of eutectic compounds dissolve into the matrix gradually,simultaneously,a new straight lamellar phase with 14H type of long period stacking ordered(LPSO) structure comes into being.Microstructure observation indicates that the lamellar phase is transformed from the un-dissolved eutectic compounds and shows a coarsening and disappearing process with annealing time prolonging.Three alloy specimens with typical microstructure after being annealed for 6,36 and 72 h were selected to age at 498 K to peak hardness.Room and elevated temperature tensile tests show that the LPSO structured phase contributes to the change of high temperature tensile properties.

引用

页码：117 / 121

页数：5

共 6 条

[1] Formation of 14H long period stacking ordered structure and profuse stacking faults in Mg–Zn–Gd alloys during isothermal aging at high temperature[J] . Michiaki Yamasaki,Minami Sasaki,Masahiko Nishijima,Kenji Hiraga,Yoshihito Kawamura.Acta Materialia . 2007 (20)
[2] Effect of Zn additions on the age-hardening of Mg–2.0Gd–1.2Y–0.2Zr alloys[J] . T. Honma,T. Ohkubo,S. Kamado,K. Hono.Acta Materialia . 2007 (12)
[3] Novel equilibrium two phase Mg alloy with the long-period ordered structure
Chino, Y
Mabuchi, M
Hagiwara, S
Iwasaki, H
Yamamoto, A
Tsubakino, H
[J]. SCRIPTA MATERIALIA, 2004, 51 (07) : 711 - 714
[4] Long period stacking structures observed inMg97Zn1Y2 alloy
Itoi, T
Seimiya, T
Kawamura, Y
Hirohashi, M
[J]. SCRIPTA MATERIALIA, 2004, 51 (02) : 107 - 111
[5] Long-period ordered structure in a high-strength nanocrystalline Mg-1 at% Zn-2 at% Y alloy studied by atomic-resolution Z-contrast STEM
Abe, E
Kawamura, Y
Hayashi, K
Inoue, A
[J]. ACTA MATERIALIA, 2002, 50 (15) : 3845 - 3857
[6] Alloy development of high toughness Mg-Gd-Y- Zn-Zr alloys. Yamada K,Okubo Y,Shiono M,Watanabe H,Kamado S,Kojima Y. Materials Transactions . 2006

← 1 →