Surface modification of TC4 Ti alloy by laser cladding with TiC+Ti powders

被引：33

作者：

张可敏 ^{[1
]}

邹建新 ^{[2
]}

李军 ^{[1
]}

于治水 ^{[1
]}

王慧萍 ^{[1
]}

机构：

[1] School of Materials Engineering,Shanghai University of Engineering Science

[2] National Engineering Research Center of Light Alloy Net Forming, School of Materials Science and Engineering,Shanghai Jiao Tong University

来源：

Transactions of Nonferrous Metals Society of China | 2010年 / 20卷 / 11期

关键词：

TC4 Ti alloy; TiC; laser cladding; segregation; hardness;

D O I：

暂无

中图分类号：

TB383.3 [];

学科分类号：

070205 ; 080501 ; 1406 ;

摘要：

Laser surface cladding was applied on a TC4 Ti alloy to improve its surface properties.Mixed TiC and Ti powders with a TiC-to-Ti mass ratio of 1:3 were put onto the TC4 Ti alloy and subsequently treated by laser beam.The microstructure and composition modifications in the surface layer were carefully investigated by using SEM,EDX and XRD.Due to melting,liquid state mixing followed by rapid solidification and cooling,a layer with graded microstructures and compositions formed.The TiC powders were completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified.The inter-dendritic areas were filled with fine α’ phase lamellae enrich in Al.Mainly due to the reduced TiC volume fraction with increasing depth,the hardness decreases with increasing depth in the laser clad layer with a maximum value of HV1400,about 4.5 times of the initial one.

引用

页码：2192 / 2197

页数：6

共 9 条

[1]

Microstructure and formation mechanism of titanium matrix composites coating on Ti-6Al-4V by laser cladding[J]. CAI Lifang, ZHANG Yongzhong, and SHI Likai National Engineering Research Center for Nonferrous Metal Composites, General Research Institute for Nonferrous Metals, Beijing 100088, China.Rare Metals. 2007(04)

[2]

Electron microscopy study of reaction layers between single-crystal WC particle and Ti–6Al–4V after laser melt injection[J] . Liqun Li,Dejian Liu,Yanbin Chen,Chunming Wang,Fuquan Li.Acta Materialia . 2009 (12)

[3]

Microstructure and tribological properties of in situ synthesized TiC, TiN, and SiC reinforced Ti 3 Al intermetallic matrix composite coatings on pure Ti by laser cladding[J] . Yuping Pu,Baogang Guo,Jiansong Zhou,Shitang Zhang,Huidi Zhou,Jianmin Chen.Applied Surface Science . 2008 (5)

[4]

Deposition of Co–Ti alloy on mild steel substrate using laser cladding[J] . Hamidreza Alemohammad,Shahrzad Esmaeili,Ehsan Toyserkani.Materials Science ＆ Engineering A . 2007 (1)

[5]

Surface modification of Ti6Al4V alloy by PIII at high temperatures: Effects of plasma potential[J] . M.M. Silva,M. Ueda,L. Pichon,H. Reuther,C.M. Lepienski.Nuclear Inst. and Methods in Physics Research, B . 2007 (1)

[6]

Solidification microstructures: recent developments, future directions[J] . W.J. Boettinger,S.R. Coriell,A.L. Greer,A. Karma,W. Kurz,M. Rappaz,R. Trivedi.Acta Materialia . 2000 (1)

[7]

Laser cladding ofTiCN/Ti coatings on Ti-6Al-4V and the calculation of thetemperature field. Yang Y L,Zhang D,Zheng Y R,et al. Optical Engineering . 2008

[8]

Microstructure and wear properties of TiCN/Ti coatings on titanium alloy by laser cladding. Yuling Yang,Duo Zhang,Wei Yan et al. Optics and Lasers in Engineering . 2010

[9]

Tailoring the surface properties of Ti6Al4V by controlled chemical oxidation. VARIOLA F,YI J H,RICHERT L,JWUEST J D,ROSEI F,NANCI A. Biomaterials . 2008

← 1 →