Effects of Ce and Sb on the microstructure and properties of AZ91D magnesium alloy prepared by the EPC process

被引：0
作者：
LI Jiqiang
机构：
来源：
Rare Metals | 2008年 / 01期
关键词：
AZ91D; Ce; Sb; microstructure; mechanical properties;
D O I：
暂无
中图分类号：
TG146.22 [];
学科分类号：
080502 ;
摘要：
The effects of small amounts of cerium and antimony additions on the microstructure and the mechanical properties of AZ91D(Mg-9Al-Zn) based alloy were researched via the expendable pattern casting(EPC) process.The results show that the microstructure is obviously refined and the tensile strength of the AZ91D based alloy at ambient temperature is significantly improved.When compared to AZ91D,the AZ91D-1.0%Ce-0.4%Sb alloy has higher ultimate tensile strength and elongation.Its ultimate tensile strength and elongation are enhanced by 39% and 47%,respectively.The morphology of the tensile fracture of the AZ91D-1.0%Ce-0.4%Sb alloy has more characteristics of quasi-cleavage.This indicates that it has had a larger plastic deformation before failure.The tensile strength and elongation decrease with the increase of Ce and Sb contents because of the coarsening and volume increase of CeSb and Al11Ce3 phases.
引用
收藏
页码：41 / 45
页数：5
相关论文
共 5 条
  • [1] Sb合金化对AE41镁合金耐热性能的影响
    刘子利
    陈照峰
    刘希琴
    陶杰
    [J]. 材料研究学报, 2006, (02) : 186 - 190
  • [2] Current and Future Use of Magnesium in the Automobile Industry[J] . Schumann S.,Friedrich Horst E..Materials Science Forum . 2003 (419)
  • [3] Effects of bismuth and antimony additions on the microstructure and mechanical properties of AZ91 magnesium alloy[J] . Yuan Guangyin,Sun Yangshan,Ding Wenjiang.Materials Science ＆ Engineering A . 2001 (1)
  • [4] Effects of Sb addition on the microstructure and mechanical properties of AZ91 magnesium alloy
    Yuan, GY
    Sun, YS
    Ding, WJ
    [J]. SCRIPTA MATERIALIA, 2000, 43 (11) : 1009 - 1013
  • [5] Effects of rare earths on the microstructure, properties and fracture behavior of Mg–Al alloys[J] . Yizhen Lü,Qudong Wang,Xiaoqin Zeng,Wenjiang Ding,Chunquan Zhai,Yanping Zhu.Materials Science ＆ Engineering A . 2000 (1)
1