Effects of Dendritic Orientation on Stress Rupture Properties of DD6 Single Crystal Superalloy

被引：0

作者：

SHI ZhenxueLI JiarongLIU ShizhongZHAO JinqianNational Key Laboratory of Science and Technology on Advanced High Temperature Structural MaterialsBeijing Institute of Aeronautical MaterialsBeijing China ^{[100095
]}

机构：

来源：

Journal of Iron and Steel Research(International) | 2011年 / 18卷 / 10期

关键词：

DD6; single crystal superalloy; stress rupture property; fracture behaviour;

D O I：

10.13228/j.boyuan.issn1006-706x.2011.10.005

中图分类号：

TG132.32 [];

学科分类号：

080502 ;

摘要：

DD6 single crystal superalloy slabs were prepared with seed method in the directionally solidified furnace with high temperature gradient.The transverse stress rupture properties and fracture behaviour of the alloy at 760 ℃/758 MPa,850 ℃/550 MPa and 980 ℃/250 MPa were investigated and compared with those of longitudinal specimens.The transverse stress rupture lives are corresponding with the longitudinal stress rupture lives at 760 ℃/758 MPa and 850 ℃/550 MPa.The transverse stress rupture lives are slightly less than the longitudinal stress rupture lives at 980 ℃/250 MPa.The fracture mechanism of the transverse stress rupture of the alloy at 760 ℃/758 MPa shows quasi-cleavage mode and the fracture mechanism at 980 ℃/250 MPa shows dimple mode,while the fracture mechanism at 850 ℃/550 MPa shows quasi-cleavage and dimple mixture mode.At higher temperature and lower stress,the microcracks are easier to initiate and interconnect in the transverse specimen than those in longitudinal specimen because there are interdendritic regions perpendicular to the axis of stress.

引用

页码：66 / 71

页数：6

共 7 条

[1] Porosity reduction by minor additions in RR2086 superalloy [J].

Chen, QZ ;

Kong, YH ;

Jones, CN ;

Knowles, DM .

SCRIPTA MATERIALIA, 2004, 51 (02) :155-160

[2]

Modelling the uniaxial creep anisotropy of nickel base single crystal superalloys CMSX-4 and RR2000 at 1023 K using a slip system based finite element approach[J] . D.W MacLachlan,G.S.K Gunturi,D.M Knowles.Computational Materials Science . 2002 (1)

[3]

Modeling of the partitioning and phase transformation temperatures of an as-cast third generation single crystal Ni-base superalloy[J] . G.E Fuchs,B.A Boutwell.Materials Science ＆ Engineering A . 2002 (1)

[4]

The role of stacking fault shear in the primary creep of[001]-oriented single crystal superalloys at 750°C and 750 MPa[J] . C.M.F. Rae,N. Matan,R.C. Reed.Materials Science ＆ Engineering A . 2001 (1)

[5]

Anisotropic creep in CMSX-4 in orientations distant from 〈001〉[J] . S.S.K Gunturi,D.W MacLachlan,D.M Knowles.Materials Science ＆ Engineering A . 2000 (1)

[6]

An FE-analysis of anisotropic creep damage and deformation in the single crystal SRR99 under multiaxial loads[J] . W Qi,W Brocks,A Bertram.Computational Materials Science . 2000 (1)

[7]

Orientation dependence of dislocation structures and deformation mechanisms in creep deformed CMSX-4 single crystals[J] . Volker Sass,Monika Feller-Kniepmeier.Materials Science ＆ Engineering A . 1998 (1)

← 1 →