Ferroelectricpropertiesofsol-gelderivedNd-dopedSrBi4Ti4O15thinfilms

被引：0

作者：

范素华 ^{[1
]}

张丰庆 ^{[1
]}

王培吉 ^{[2
]}

任艳霞 ^{[3
]}

机构：

[1] Department of Materials Science and Engineering, Shandong Jianzhu University

[2] Department of Science, University of Jinan

[3] Jiyuan Vocational and Technical College

来源：

Journal of Rare Earths | 2008年 / 04期

关键词：

SrBi4Ti4O15 thin films; sol-gel method; ferroelectric properties; rare earths;

D O I：

暂无

中图分类号：

TB383.2 [];

学科分类号：

070205 ; 080501 ; 1406 ;

摘要：

Neodymium-doped strontium bismuth titanate (SrBi4-xNdxTi4O15) ferroelectric thin films were fabricated using the sol-gel method on Pt/Ti/SiO2/Si substrates. The influence of Nd content on the microstructure and ferroelectric properties of SrBi4–xNdxTi4O15 thin films were systematically studied. The results indicated that the SrBi3.88Nd0.12Ti4O15 (SBNT0.12) thin films had better ferroelectric properties, with a remanent polarization of (2Pr) of 34.3 μC/cm2 and a coercive field (2Ec) of 220 kV/cm. This could be attributed to the fact that SBNT0.12 ferroelectric thin films consisted of more and larger ball-like grains, approximately 150–200 nm, with structure distortion, which greatly contributed to the improvement of the ferroelectric properties of the films. Furthermore, the film exhibited a good fatigue resistant property. The value of 2Pr after 1010 switching cycles did not change significantly. The SrBi3.88Nd0.12Ti4O15 films were promising candidates for the application of FeRAMs.

引用

页码：575 / 578

页数：4

共 3 条

[1] Mo掺杂SrBi4Ti4O15陶瓷的铁电介电性能 [J].

金灿 ;

朱骏 ;

毛翔宇 ;

何军辉 ;

陈小兵 .

物理学报, 2006, (07) :3716-3720

[2] Effects of Excess Bismuth on Structure and Properties of SrBi4Ti4O15 Ceramics [J].

Fan Suhua ;

Chen Wen ;

Zhang Fengqing ;

Hu Guangda .

JOURNAL OF RARE EARTHS, 2007, 25 :317-321

[3]

Electrical properties of neodymium doped CaBi 4 Ti 4 O 15 ceramics[J] . Jiangtao Zeng,Yongxiang Li,Dong Wang,Qingrui Yin.Solid State Communications . 2005 (9)

← 1 →