Rise of correlated dislocations in nanotwinned metals against fatigue

被引：0

作者：

Yongjun Tian

机构：

[1] StateKeyLaboratoryofMetastableMaterialsScienceandTechnology,YanshanUniversity

来源：

Science China Materials | 2018年 / 61卷 / 01期

关键词：

Rise of correlated dislocations in nanotwinned metals against fatigue;

D O I：

暂无

中图分类号：

TG425 [钎焊材料];

学科分类号：

080201 ; 080503 ;

摘要：

<正>When a metal is subject to cyclic loading with cyclic stress values much lower than its tensile strength,fatigue occurs due to accumulative and irreversible damages developed in the microstructure,causing service failure of the metal workpiece or even fatal disaster in the worst cases.To develop materials with higher fatigue limit and longer fatigue life relies on reducing or suppressing these

引用

页码：127 / 128

页数：2

共 10 条

[1]

History-independent cyclic response of nanotwinned metals. Pan Q,Zhou H,Lu Q,et al. Nature . 2017

[2]

Detwinning, damage and crack initiation during cyclic loading of Cu samples containing aligned nanotwins[J] . C.J. Shute,B.D. Myers,S. Xie,S.-Y. Li,T.W. Barbee,A.M. Hodge,J.R. Weertman. &nbspActa Materialia . 2011 (11)

[3]

Cyclic deformation and fatigue properties of very fine-grained metals and alloys[J] . &nbspInternational Journal of Fatigue . 2009 (9)

[4]

Mechanical properties of nanocrystalline materials[J] . M.A. Meyers,A. Mishra,D.J. Benson. &nbspProgress in Materials Science . 2005 (4)

[5] Cyclic deformation behavior of ultra-fine grained copper processed by accumulative roll-bonding [J].

Kwan, Charles C. F. ;

Wang, Zhirui .

FATIGUE 2010, 2010, 2 (01) :101-110

[6]

Stabilizing nanostructures in metals using grain and twin boundary architectures. Lu K. Nat.Rev.Mater . 2016

[7]

Strengthening Materials by Engineering Coherent Internal Boundaries at the Nanoscale. Lu K,Lu L,Suresh S. Science . 2009

[8]

Fatigue behavior of columnar-grained Cu with preferentially oriented nanoscale twins[J] . Q.S. Pan,Q.H. Lu,L. Lu. &nbspActa Materialia . 2012

[9]

Strain-controlled cyclic stability and properties of Cu with highly oriented nanoscale twins[J] . Q.S. Pan,L. Lu. &nbspActa Materialia . 2014

[10]

Deformation twinning[J] . J.W. Christian,S. Mahajan. &nbspProgress in Materials Science . 1995 (1)

← 1 →