Fractographic analysis of strontium-modified al-si alloys

被引：0

作者：

Hren I. ^{[1
]}

Svobodova J. ^{[1
]}

机构：

[1] Faculty of Mechanical Engineering, J. E. Purkyne University in Usti nad Labem, Pasteurova 3334/7, Usti nad Labem

来源：

Manufacturing Technology | 2018年 / 18卷 / 06期

关键词：

AlSi7Mg0.3; Beryllium; Microstructure; Modification; Strontium;

D O I：

10.21062/ujep/198.2018/a/1213-2489/mt/18/6/900

中图分类号：

学科分类号：

摘要：

The research described in this contribution is focuses on fractographic analysis of the fracture area of AlSi7Mg0.3 alloy with modified strontium. Modification is an effective tool for improving the mechanical properties of aluminum alloys and affecting the microstructure of the material. The aim of the paper is to revise the microstructure of the modified AlSi7Mg0.3 alloy and to determine its strength properties. Within the experiment, the character of the refraction was evaluated and the presence of foreign particles and elements in the material fracture was monitored. Optical microscopy identified structural parameters of the castings just below the fracture surface as well as the course of the fracture line. Using a scanning electron microscope, the fracture area of the sample was analyzed, the EDS analysis was performed and the results of these analyzes were evaluated. An increased number of O, C and F elements occurred on the surface of the samples. The occurrence of these elements most likely results in a material breakage, which also confirms the results achieved by the static tensile test. On the basis of the obtained results from the analyzes carried out, the mechanisms of the breach were determined. © 2018. Published by Manufacturing Technology.

引用

页码：900 / 905

页数：5

共 13 条

[1]

Michna S., Et al., Encyklopedie hliníku, 1, (2005)

[2]

Bolibruchova D., Tillova E., Zlievarenské zliatiny Al-Si, (2005)

[3]

Mondolfo L.F., Aluminium Alloys, Structure and Properties, (1979)

[4]

Davidson C.J., Et al., The Effect of solution heat Treatment Time on Fatigue Properties of an Al-Si-Mg Casting Alloy, FFEMS, 25, pp. 223-230, (2002)

[5]

Tillova E., Chalupova M., Hurtalova L., Durinikova E., Quality Control of Microstructure in Recycled Al-Si Cast Alloys, Manufacturing Technology, 11, 11, pp. 70-76, (2011)

[6]

Naprstkova N., Cais J., Svobodova J., The Effect of Modification by Strontium of the AlSi7Mg0.3 Alloy on the Surface Roughness, Manufacturing Technology, 13, 3, pp. 380-384, (2013)

[7]

Michna S., Naprstkova N., Lukac I., Mechanical Properties Optimization of AlSi12CuMgNi Alloy by Heat Treatment, Metallofizika i Noveishie Teknologii, 11, (2011)

[8]

Lipinski T., Microstructure and Mechanical Properties of the AlSi13Mg1CuNi Alloy with Ecological Modifier, Manufacturing Technology, 11, 11, pp. 40-44, (2011)

[9]

Honzatko R., Michna S., Cais J., The Influence of Porosity on Mechanical Propertis of Casts Produced from Al-Si Alloys, Manufacturing Technology, 13, 3, (2013)

[10]

Michna S., Lukac I., Praktická fraktografie, (2012)

← 1 2 →