Effects of sol proportion on mechanical properties of carbon fiber reinforced carbon aerogel insulation composites

被引：0

作者：

Yang X. ^{[1
,2
]}

Feng J. ^{[2
]}

Jiang Y. ^{[2
]}

Zhang Z. ^{[1
]}

Feng J. ^{[2
]}

机构：

[1] School of Materials Science and Engineering, Xi'an University of Technology, Xi'an

[2] Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha

来源：

Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2016年 / 33卷 / 06期

关键词：

Carbon aerogel; Composites; Densities; Mechanical properties; Microstructure;

D O I：

10.13801/j.cnki.fhclxb.20151209.005

中图分类号：

学科分类号：

摘要：

Carbon fiber reinforced carbon aerogel composites were prepared by impregnating the fiber preform, gel aging, supercritical drying and carbonization. Resorcinol (R)-furfural (F) alcohol sol was synthesized by isopropanol (I) as solvent, hexamethylenetetramine (H) as catalyst. The effects of sol proportion on densities, microstructures and mechanical properties of carbon fiber reinforced carbon aerogel insulation composites were investigated. The results show that the densities of carbon fiber reinforced carbon aerogel insulation composites decrease gradually, the pores diameter and the amount of large pores in matrix carbon aerogels and the interface formed with carbon fiber increase, the strength of carbon fiber reinforced carbon aerogel insulation composites decreases with the increases of amount of substance ratio for isopropanol and resorcinol. When isopropanol and resorcinol amount of substance ratio increases from 18 to 28, the compressive strength decreases from 2.498 MPa (strain 10%)to 0.716 MPa (strain 10%), tensile strenghth decreases from 2.019 MPa to 1.001 MPa, bending strength decreases from 3.984 MPa to 1.818 MPa. The densities of carbon fiber reinforced carbon aerogel insulation composites increases firstly and then decreases, the pores diameter and the the amount of large pores in matrix carbon aerogels and interface formed with carbon fiber decreases firstly and then increases, the strength of carbon fiber reinforced carbon aerogel insulation composites increases fistly and then decreases with the increase of amount of substance ratio for hexamethylenetetramine and resorcinol. The densities and the strength of carbon fiber reinforced carbon aerogel insulation composites are biggest when amount of substance ratio for hexamethylenetetramine and resorcinol is 0.008 5, the compressive strength is 1.066 MPa (strain 10%), the tensile strenghth is 1.256 MPa, bending strength is 3.556 MPa. © 2016, BUAA Culture Media Group Ltd. All right reserved.

引用

页码：1251 / 1258

页数：7

共 14 条

[1]

Feng J.Z., Zhang C.R., Feng J., Carbon fiber reinforced carbon aerogel composites for thermal insulation prepared by soft reinforecement, Materials Letters, 67, 1, pp. 266-268, (2012)

[2]

Feng J., Feng J.Z., Jiang Y.G., Et al., Thermal tansport in carbon aerogels and their applications in thermal protection system, Arospace Materials&Technology, 42, 2, (2012)

[3]

Hrubesh L.W., Lightweight, high strength carbon aerogel composites and method of fabrication

[4]

Yang J., Li S.K., Luo Y.M., Et al., Compressive properties and fracture behavior of ceramic fiber-reinforced carbon aerogel under quasi-static and dynamic loading, Carbon, 49, 5, pp. 1542-1549, (2011)

[5]

Liu B., Zou J.F., Zhan W.C., Et al., A fiber reinforced carbon aerogel composite and it's preparation method

[6]

Fu R.W., Zheng B., Liu J., Et al., Fabrication of activated carbon fibers/carbon aerogels composites by gelation and supercritical drying in isopropanol, Journal of Materials Research, 18, 12, pp. 2765-2773, (2003)

[7]

Leventis N., Chandrasekaran N., Sadekar A.G., Et al., The effect of compactness on the carbothermal conversion of interpenetrating metal oxide/resorcinol-formaldehyde nanoparticle networks to porous metals and carbides, Journal of Materials Chemistry, 20, 35, pp. 7456-7471, (2010)

[8]

Xu T.H., Structure evolutions and modifications of SiOC ceramics dericed from polysiloxane, (2011)

[9]

Feng J.Z., Zhang C.R., Feng J., Et al., Carbon aerogel composites prepared by ambient drying and using oxidized polyacrylonitrile fibers as reinforcements, ACS Applied Materials & Interfaces, 3, 12, pp. 4796-4803, (2011)

[10]

Fu R.W., Wu D.C., Method for preparing organic aerogel and carbon aerogel by atmospheric drying method

← 1 2 →