Effect of initial damage on fatigue performance of welded joints

被引：0

作者：

Jie, Zhiyu ^{[1
]}

Li, Yadong ^{[1
]}

Wei, Xing ^{[1
]}

机构：

[1] School of Civil Engineering, Southwest Jiaotong University, Chengdu

来源：

Xinan Jiaotong Daxue Xuebao/Journal of Southwest Jiaotong University | 2015年 / 50卷 / 03期

关键词：

Damage curve; Damage variable; Fatigue life; Initial damage; Welded joint;

D O I：

10.3969/j.issn.0258-2724.2015.03.006

中图分类号：

学科分类号：

摘要：

In order to investigate the effect of initial damage of a welded joint on its fatigue life and damage evolution, adopting the damage variable based on crack size from the damage mechanics, two common fatigue damage evolution models, the Chaboche model and the Lemaitre model, were used to discuss the effect of the initial damage on the fatigue life and damage variable of the welded joint, and a concept of fatigue life reduction factor that is based on the initial damage was proposed. Then, the fatigue life reduction factors and fatigue damage curves under different initial damage were obtained from a non-carrying fillet welded joint in a case study. The results show that when the initial damage is less than 0.055 or 0.002, its effect on the fatigue life can be ignored in both the Chaboche model and the Lemaitre model. The Lemaitre model is more sensitive to the initial damage than the Chaboche model, and the Chaboche model is more appropriate to describe fatigue damage evolution of welded joints. ©, 2015, Science Press. All right reserved.

引用

页码：423 / 427

页数：4

共 13 条

[1]

Cheng G.X., Zuo J.Z., Lou Z.W., Et al., Continuum damage model of low-cycle fatigue and fatigue damage analysis of welded joint, Engineering Fracture Mechanics, 55, 1, pp. 155-161, (1996)

[2]

Wu H., Guo H., Gao D., Fractal damage evolution model of low-cycled fatigue in welded joint, Transactions of the China Welding Institution, 24, 1, pp. 88-90, (2003)

[3]

Li S., Ge H., A model of S-N curve considering pre-damage of material, Journal of Ningxia Institute of Technology, pp. 385-387, (1996)

[4]

Zhou T., Chan T.H., Fatigue crack growth and fatigue life evaluation for welded steel bridge members with initial crack, Journal of Ship Mechanics, 13, 1, pp. 91-99, (2009)

[5]

Liu X., Guo H., Wang B., Et al., Study on high cycle fatigue fractal damage model of TC11 alloy welded joint, Journal of Aerospace Power, 26, 2, pp. 355-361, (2011)

[6]

Shi M., Jiang M., An investigation on the ductile damage evolution law of high-cycle fatigue, Engineering Fracture Mechanics, 46, 3, pp. 393-397, (1993)

[7]

Wu H., A method of fatigue life forecasting of damage fractal evolution on Ti alloy welded joints, Materials for Mechanical Engineering, 32, 11, pp. 86-89, (2008)

[8]

Yu B., Qiu H., Wang H., Et al., Experimental research on fatigue behavior and damage development of welded conformation of orthotropic steel bridge deck, China Journal of Highway and Transport, 26, 9, pp. 64-69, (2009)

[9]

Shen W., Peng L., Evolution equations of fatigue damage and estimate of fatigue life: application of continuum damage mechanics, Journal of Mechanical Strength, 16, 2, pp. 52-57, (1994)

[10]

Fang H., Jia X., A new method of damage mechanics for estimating the fatigue life of offshore oil steel structure, Oil Field Equipment, 6, pp. 10-14, (1990)

← 1 2 →