Thermal Stability of Residual Stress, Microstructure, and Mechanical Property in Shot-Peened CNT/Al-Cu-Mg Composites

To investigate the thermal stability of a shot-peened specimen and ensure the reliability operation under high temperatures, CNT/Al-Cu-Mg composites were treated by shot peening (SP) and the isothermal aging treatment. The heating temperatures were 100, 150, 200, and 250 degrees C. Changes in surface residual stress and the distribution along the depth were investigated. The microstructure changes were analyzed by XRD and observed by TEM. Changes in mechanical properties were characterized by microhardness. The results show that the compressive residual stress (CRS) release and the microstructure changes mainly occurred at the initial stage of heating treatment. After 128 min of isothermal aging treatment at 250 degrees C, the surface CRS released 91.9% and the maximum CRS released 80.9%, the surface domain size increased by 222%, and the microstrain and microhardness decreased by 49% and 27.3%, respectively. The reinforcement effect introduced by SP basically disappeared. A large number of second-phase particles, such as CNT, Al2Cu, and Al4C3, were anchored at grain boundaries, hindering dislocation movement and enhancing the thermal stability of the material. Isothermal aging treatment at 100 degrees C and 150 degrees C for a duration of 32 min is a reliable circumstance for maintaining SP reinforcement.