Fatigue behavior of as-cast and heat-treated Mg-Gd-Y-Er alloy at room temperature

被引:0
作者
S, Sudharsan [1 ]
A, Raja Annamalai [2 ]
机构
[1] School of Mechanical Engineering, Vellore Institute of Technology, Tamil Nadu, Vellore
[2] Centre for Innovative Manufacturing Research, Vellore Institute of Technology, Tamil Nadu, Vellore
关键词
Fatigue; Fractography; Heat treatment; Mg alloy;
D O I
10.1016/j.engfailanal.2025.109652
中图分类号
学科分类号
摘要
In this study, the fatigue behavior of the Mg-Gd-Y-Er alloy has been investigated under cast, T4, and T6-treated conditions. The high-cycle fatigue (HCF) test was conducted at room temperature, with a frequency of 15 Hz and a stress ratio of 0.1. The as-cast and T4-treated samples exhibit a fatigue strength of 51 MPa at 105 cycles. At the same time, the T6-treated samples show fatigue strengths of 55 MPa and 68 MPa, which are 7 % and 33 % higher than the fatigue strength of the as-cast alloy. The fractured surface reveals the brittle mode of fracture in both conditions. © 2025 Elsevier Ltd
引用
收藏
相关论文
共 22 条
  • [21] Tokaji K., Kamakura M., Ishiizumi Y., Hasegawa N., Fatigue behavior and fracture mechanism of a rolled AZ31 magnesium alloy, Int. J. Fatigue, 26, 11, pp. 1217-1224, (2004)
  • [22] Gao L., Chen R., Han E., Fracture behavior of high strength Mg-Gd-Y-Zr magnesium alloy, Trans. Nonferrous Met. Soc. Chin., 20, 7, pp. 1217-1221, (2010)