Mechanical Properties and Tribological Study of Bottom Pouring Stir-Cast A356 Alloy Reinforced with Graphite Solid Lubricant Extracted from Corn Stover

The present work epitomises extracting the graphite (Gr) solid lubricant from the corn stover. The extracted Gr was incorporated as reinforcement in the A356 alloy (Al-7Si), and the effect of the Gr particles on the mechanical and tribological properties was investigated. In spite of this, the input process parameters for the dry sliding wear test at room temperature against the EN31 steel disc were optimised through ANOVA analysis. The fabricated A359-X wt% (X = 0, 2.5, 5, 7.5) composite through bottom pouring stir casting techniques was analysed microstructurally by using XRD and FESEM analysis. The micro Brinell hardness and tensile strength were investigated per ASTME10 and ASTME8M standards. A wear test was performed for the composite pins against the EN31 steel disc according to ASTM G99 specifications. The XRD analysis results depict the presence of carbon (C), aluminium (Al), and silicon (Si) in all the wt% of the Gr reinforcement. However, along with the elements, the Al2Mg peak was confirmed for the A356-7.5 wt% Gr composite and the corresponding cluster element was confirmed in FESEM analysis. The maximum micro Brinell hardness of 92 BHN and U.T.S of 123 MPa and % elongation of 7.11 was attained at 5 wt% Gr reinforcement due to uniform Gr dispersion in the A356 alloy. Based on the ANOVA analysis, the optimal process parameters were obtained at 20 N applied load, 1 m/s sliding velocity, and 1000 m sliding distance for the optimal wear rate of 0.0052386 g/km and 0.364 COF.