Mechanical Properties and Corrosion Resistance of La2O3/A356 Composites Fabricated by Ultrasonic-Assisted Casting

被引：0

作者：

Wan, Hao ^{[1
]}

Shuai, Luming ^{[1
]}

Ling, Lishibao ^{[1
]}

Hu, Zhi ^{[1
]}

Yan, Hong ^{[1
]}

机构：

[1] Nanchang Univ, Sch Adv Mfg, Nanchang 330031, Peoples R China

来源：

METALS | 2025年 / 15卷 / 02期

基金：

中国国家自然科学基金;

关键词：

La2O3/A356; composites; mechanical properties; corrosion resistance; strengthening mechanism; IN-SITU; TENSILE PROPERTIES; FRACTURE-BEHAVIOR; ALUMINUM; MICROSTRUCTURE; ALLOY; STIR; MG;

D O I：

10.3390/met15020184

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Mechanical properties and corrosion resistance of La2O3/A356 composites with different contents of La2O3 were investigated by optical microscopy, X-ray diffractometry, scanning electron microscopy, electrochemical tests, and immersion corrosion tests. The results show that the addition of La2O3 refined the alpha-Al phase of the A356 matrix, and the long stripe-like Si phase and beta-Al5FeSi phase were transformed into short rod-like forms. The La2O3/A356 composites with 1.0 wt.% La2O3 exhibited the most optimal mechanical properties and corrosion resistance. The yield strength, ultimate tensile strength, and elongation of La2O3/A356 composites with 1.0 wt.% La2O3 were higher than those of the matrix. The results of electrochemical experiments and the immersion corrosion test show that the corrosion potential of La2O3/A356 composites with 1.0 wt.% La2O3 was 72 mV higher than that of the matrix, the corrosion current density was 84.8% lower than that of the matrix, and the impedance Z was improved by 59.1% compared to the matrix. The addition of La2O3 improved the mechanical properties of the A356 matrix by refining the grains, inhibiting the nucleation of eutectic Si, and promoting the twinning growth mechanism. Moreover, the effect of La2O3 on the micro-galvanic corrosion behavior of A356 was discussed.

引用

页数：16

共 41 条

[1] Wu W.Q., Gong M.Y., Wei B.Q., Misra A., Wang J., Atomistic modeling of interface strengthening in Al-Si eutectic alloys, Acta Mater, 225, (2022)
[2] Xi H.L., Xiao W.L., Li H., Fu Y., Yi G., Qie J., Ma X., Ma C., Effects of submicron-sized TiC particles on the microstructure modification and mechanical properties of Al-Si-Mg alloy, J. Alloys Compd, 968, (2023)
[3] Pramod S.L., Prasada Rao A.K., Murty B.S., Bakshi S.R., Effect of Sc addition on the microstructure and wear properties of A356 alloy and A356-TiB2 in situ composite, Mater. Des, 78, pp. 85-94, (2015)
[4] Garza Elizondo G.H., Elsharkawi E.A., Samuel A.M., Doty H.W., Samuel F.H., Effects of Alloying Elements Additions on Ambient Temperature Performance of Al–Si–Cu–Mg Base Alloys, Int. J. Met, 15, pp. 1385-1401, (2021)
[5] Liao H.C., Lu L.Z., Li G.J., Huang Y.L., Yang L.L., Guo H.T., Wu F., Influence of minor addition of La and Ce on the ageing precipitation behavior of Sr-modified Al-7Si-0.6Mg alloy, Mater. Today Commun, 39, (2024)
[6] Liang Y.G., Cui C.X., Geng H.T., Liu L., Cui S., Yang S.C., Effects of In-Situ BaB6/Al Composite Inoculant on the Mechanical and Corrosion Behavior of Al-7Si-0.3Mg Alloy, Met. Mater. Int, 29, pp. 968-982, (2022)
[7] Heusler L., Schneider W., Influence of alloying elements on the thermal analysis results of Al-Si cast alloys, J. Light Met, 2, pp. 17-26, (2002)
[8] Yang Y., Zhou W.F., Tong Z.P., Chen L., Yang X.Q., Larson E.A., Ren X.D., Electrochemical Corrosion Behavior of 5083 Aluminum Alloy Subjected to Laser Shock Peening, J. Mater. Eng. Perform, 28, pp. 6081-6091, (2019)
[9] Kang J., Su R., Wu D.Y., Liu C.H., Li T., Wang L.S., Narayanaswamy B., Synergistic effects of Ce and Mg on the microstructure and tensile properties of Al-7Si-0.3Mg-0.2Fe alloy, J. Alloys Compd, 796, pp. 267-278, (2019)
[10] Amer S.M., Glavatskikh M.V., Barkov R.Y., Khomutov M.G., Pozdniakov A.V., Phase composition and mechanical properties of Al-Si based alloys with Yb or Gd addition, Mater. Lett, 320, (2022)

← 1 2 3 4 5 →