Effect of Reduction in Heat Input on the Behavior of 316LSi Thin Wall Fabricated by Wire Arc Additive Manufacturing

被引:0
作者
Aberkane, Salima [1 ,2 ]
Mehdi, Brahim [1 ]
Badji, Riad [2 ]
Attallah, Moataz [3 ]
Fenineche, Nouredine [4 ]
Alili, Baya [1 ]
机构
[1] Univ Sci & Technol Houari Boumediene USTHB, Fac Phys, Mat Phys Lab, BP 32, Algiers 16111, Algeria
[2] Res Ctr Ind Technol CRTI, POB 64, Algiers 16014, Algeria
[3] Univ Birmingham, Sch Met & Mat, Birmingham B15 2TT, England
[4] Univ Bourgogne Franche Comte, UTBM, CNRS, ICB UMR 6303, F-90010 Belfort, France
关键词
AISI; 316LSi; corrosion; dislocation density; heat input; microstructure; WAAM process; MECHANICAL-PROPERTIES; STAINLESS-STEEL; CORROSION-RESISTANCE; MICROSTRUCTURE; SOLIDIFICATION; METAL;
D O I
10.1007/s11665-025-11065-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this work, the effect of heat input reduction on the microstructure and the quality of 316LSi thin walls fabricated by wire arc additive manufacturing was investigated. During the building of the walls, the heat input was reduced from 208.5 to 77.7 J/mm. The interpass temperature increased when using 208.5 J/mm until reaching 650 degrees C and then decreased to remain stable around 600 degrees C for the other heat input levels (101.3, 89.6 and 77.7 J/mm). The study revealed the close dependency of the wall quality on both corrosion resistance and dislocation density values impacted by grain orientation. The x-ray diffraction analysis showed a substantial impact of the (220) and (111) grain orientations on the dislocation density values. A decrease in the dislocation density values accompanied with a tendency toward their isotropic distribution was noticed for a heat input level of 101.3 J/mm. This isotropic distribution was accompanied with an improvement of the corrosion resistance with the best R-p value of 1.49 x 10(4) (Omega.cm(-2)). It was also found that the heat input value of 101.3 J/mm resulted in the best tensile properties of the fabricated walls. The strain hardening behavior analysis revealed that the Hockett-Sherby model gave the best agreement with the experimental tensile data.
引用
收藏
页数:14
相关论文
共 53 条
  • [11] Review on residual stresses in metal additive manufacturing: formation mechanisms, parameter dependencies, prediction and control approaches
    Chen, Shu-guang
    Gao, Han-jun
    Zhang, Yi-du
    Wu, Qiong
    Gao, Zi-han
    Zhou, Xin
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 17 : 2950 - 2974
  • [12] Strengthening mechanisms in selective laser melted 316L stainless steel
    Chen, Siqi
    Ma, Guoqiang
    Wu, Guilin
    Godfrey, Andrew
    Huang, Tianlin
    Huang, Xiaoxu
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 832
  • [13] Initiation and growth mechanisms for weld solidification cracking
    Coniglio, N.
    Cross, C. E.
    [J]. INTERNATIONAL MATERIALS REVIEWS, 2013, 58 (07) : 375 - 397
  • [14] Cunningham C.R., 2019, FABR 2019 P 30 ANN I
  • [15] Geometry of dimples and its correlation with mechanical properties in austenitic stainless steel
    Das, Arpan
    Tarafder, Soumitra
    [J]. SCRIPTA MATERIALIA, 2008, 59 (09) : 1014 - 1017
  • [16] DeLong WT., 1975, Weld. J, V7, P75
  • [17] Influence of heat input on microstructure and mechanical behaviour of austenitic stainless steel 316L processed in wire and arc additive manufacturing
    Gowthaman, P. S.
    Jeyakumar, S.
    Sarathchandra, D. T.
    [J]. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART E-JOURNAL OF PROCESS MECHANICAL ENGINEERING, 2023, 237 (02) : 149 - 161
  • [18] Effect of Strain Hardening on Wear and Corrosion Resistance of 316L Austenitic Stainless Steel
    Huang, Jiaqi
    Sun, Guoqing
    Peng, Jian
    Wu, Wangping
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (16) : 8108 - 8121
  • [19] Formation mechanism of vermicular and lacy ferrite in austenitic stainless steel weld metals
    Inoue, H
    Koseki, T
    Ohkita, S
    Fuji, M
    [J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2000, 5 (06) : 385 - 396
  • [20] Rearrangements of dislocations during continuous heating of deformed β-TiNb alloy observed by in-situ synchrotron X-ray diffraction
    Ivanov, Ivan V.
    Emurlaev, Kemal I.
    Lazurenko, Daria V.
    Stark, Andreas
    Bataev, Ivan A.
    [J]. MATERIALS CHARACTERIZATION, 2020, 166