Improving the water resistance of gypsum-based building materials with slag activated by calcium oxide

被引：1
作者：
Feng, Chunhua [1 ]
Wang, Yisen [1 ]
Wang, Luwei [1 ]
Zhao, Xiaomeng [1 ]
Zhang, Wenyan [1 ]
Zhu, Jianping [1 ]
Du, Mingxing [1 ]
机构：
[1] Henan Polytech Univ, Sch Mat Sci & Engn, Jiaozuo 454003, Peoples R China
来源：
JOURNAL OF CO2 UTILIZATION | 2024年 / 90卷
关键词：
Gypsum waterproofing; Carbon emissions; Alkali-activated slag; CEMENT; HYDRATION;
D O I：
10.1016/j.jcou.2024.102996
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
The water resistance of building gypsum products was poor, which led to certain limitations in their application. In this paper, calcium oxide and slag were added to building gypsum to study the effect of calcium oxide alkali activation of slag on the water resistance of building gypsum. Low-field nuclear magnetic resonance technology, X-ray diffraction technology, and other modern testing techniques were employed to investigate the hydration process and water resistance mechanism of building gypsum. It was found that the use of calcium oxide to activate slag could effectively enhance the water resistance of building gypsum. It was discovered that when the dosage of slag was 50 % and the dosage of calcium oxide was 2 % of the slag, the softening coefficient of building gypsum after 28 days was increased from 0.26 to 0.93. When calcium oxide was used to activate slag, not only was C-(A)-S-H gel formed, but also more ettringite was produced. The formation of ettringite and C-(A)-S-H gel was greatly influenced by the presence of water. These substances were found to have stronger water resistance compared to gypsum crystals. The structural system built by the interlocking of these substances significantly enhanced the water resistance of the samples, thereby improving the water resistance of building gypsum blocks. Simultaneously, at a lower addition rate (2 % relative to the amount of slag), as the replacement amount of slag increased, the cost of the samples and the carbon emissions were also relatively reduced.
引用
收藏
页数：12
相关论文
共 62 条
  • [1] Xie Z., Liu X., Zhang Z., Wei C., Gu J., Application of the industrial byproduct gypsum in building materials: a review, Materials, 17, (2024)
  • [2] Jiang Z.-Y., Sun X.-P., Luo Y.-Q., Fu X.-L., Xu A., Bi Y.-Z., Recycling, reusing and environmental safety of industrial by-product gypsum in construction and building materials, Constr. Build. Mater., 432, (2024)
  • [3] Zhang X., Wang Z., Mao J., Huang W., Preparation technology of lightweight high-strength desulphurized gypsum block, J. Phys.: Conf. Ser., 2706, (2024)
  • [4] Zhou J., Li X., Zhao Y., Shu Z., Wang Y., Zhang Y., Shen X., Preparation of paper-free and fiber-free plasterboard with high strength using phosphogypsum, Constr. Build. Mater., 243, (2020)
  • [5] Silva T.K.D.S., Ferraz A.D.V., dos Anjos D.S.C., Estudo da impermeabilização do gesso de revestimento através da síntese do compósito hidrofóbico de gesso/silicone, Matéria (Rio J.), 27, (2022)
  • [6] Jiang Q., Huang J., Ma B., Yang Z., Zhang T., SiO2/silicone hybrid superhydrophobic coating on gypsum-based materials with self-cleaning and moisture resistance, J. Sol. -Gel Sci. Technol., 96, pp. 207-218, (2020)
  • [7] He T., Kang Z., Chen C., Influence of sodium methyl silicate on waterproof property of desulfurized gypsum block, Jianzhu Cailiao Xuebao/J. Build. Mater., 24, pp. 247-253, (2021)
  • [8] Cao J.-Y., Li J.-P., Jiang Y.-M., Wang S.-L., Ding Y., Oh W.-C., Improvement in water resistance of desulfurized gypsum by novel modification of silicone oil paraffin composite emulsion-based waterproofing agent, J. Korean Ceram. Soc., 56, pp. 558-565, (2019)
  • [9] Kovler K., Enhancing water resistance of cement and gypsum-cement materials, J. Mater. Civ. Eng., 13, pp. 349-355, (2001)
  • [10] Camarini G., De Milito J.A., Gypsum hemihydrate–cement blends to improve renderings durability, Constr. Build. Mater., 25, pp. 4121-4125, (2011)
1234567