Ultrastable Ti@Ir core-shell catalyst with low iridium loading for water electrolysis at industrial-level current density

被引：2

作者：

Yang, Jiahao ^{[1
,2
]}

Shi, Zhaoping ^{[1
,2
]}

Wang, Yibo ^{[1
,2
]}

Wu, Hongxiang ^{[1
,2
]}

Ni, Jing ^{[1
,2
]}

Wang, Pengbo ^{[1
,2
]}

Xiao, Meiling ^{[1
,2
,3
]}

Liu, Changpeng ^{[1
,2
,3
]}

Xing, Wei ^{[1
,2
,3
]}

机构：

[1] Univ Sci & Technol China, Sch Appl Chem & Engn, Hefei 230026, Peoples R China

[2] Chinese Acad Sci, State Key Lab Electroanalyt Chem, Lab Adv Power Sources, Changchun 130022, Peoples R China

[3] Chinese Acad Sci, HK Joint Lab Hydrogen Energy, Changchun 130022, Peoples R China

来源：

CHEMICAL ENGINEERING JOURNAL | 2025年 / 506卷

基金：

国家重点研发计划;

关键词：

Proton exchange membrane water electrolysis; Oxygen evolution reaction; Core-shell nanostructured catalyst; Metallic titanium core; Iridium shell; OXYGEN EVOLUTION; HIGH-PERFORMANCE; SUPPORT; ELECTROCATALYSTS; ASSEMBLIES; ELECTRODES; OXIDATION;

D O I：

10.1016/j.cej.2025.160118

中图分类号：

X [环境科学、安全科学];

学科分类号：

08 ; 0830 ;

摘要：

Despite proton exchange membrane water electrolysis (PEMWE) being a commercially viable method for high-purity hydrogen production, the development of active and robust anode electrocatalysts with reduced iridium loading under high current density conditions remains highly challenging. Here, we report a core-shell nanostructured catalyst with a metallic titanium core uniformly covered by Ir nanoparticles (Ti@Ir). The spontaneously formed TiOx layer can effectively disperse Ir nanoparticles via interfacial Ti-O-Ir bonds, which in turn increases the oxidation state of Ir towards activated lattice oxygen reactivity, as confirmed by in-situ differential electrochemical mass spectrometry (DEMS). As a result, the Ti@Ir exhibits an overpotential of only 272 mV to reach 10 mA cm(-2), 17 mV lower than non-supported Ir nanoparticles, and a 3.82-fold higher mass activity at 1.53 V. Moreover, the Ti@Ir catalyst demonstrates strong stability during a 100-hour test at 10 mA cm(-2). Detailed analysis reveals that the oxidation of iridium close to the titanium core is suppressed. The huge potential for practical application is further confirmed in a PEMWE prototype, with a low iridium loading of 0.5 mg(Ir) cm(-2), significantly lower than the typical 2 similar to 4 mg(Ir) cm(-2) required for traditional catalysts. This Ti@Ir catalyst achieves a cell voltage of 1.858 V at an industrial-level current density of 2 A cm(-2) and maintains stable operation for 1800 h with an exceptionally low voltage degradation rate of only 1.252 mu V h(-1).