Improving strength-ductility of Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr magnesium alloy due to bimodal LPSO and <c + a> dislocations

被引:0
作者
Zhang, Xiaohua [1 ]
Shi, Yuan [1 ]
Li, Jiaqi [1 ]
Yue, Hongyan [1 ]
Li, Chao [1 ]
Guo, Siming [2 ]
Chen, Qiang [3 ]
机构
[1] Harbin Univ Sci & Technol, Sch Mat Sci & Chem Engn, Harbin 150040, Peoples R China
[2] Binary Univ Management & Entrepreneurship, Sch Binary Grad, Puchong 47100, Malaysia
[3] Southwest Technol & Engn Res Inst, Chongqing 400039, Peoples R China
关键词
Rare earths; Magnesium alloy; Solution treatment; LPSO; Texture; Mechanical properties; ZN-ZR ALLOY; STACKING ORDERED PHASE; MECHANICAL-PROPERTIES; MG-GD; DYNAMIC RECRYSTALLIZATION; Y-ALLOY; HOT COMPRESSION; MICROSTRUCTURE; BEHAVIOR; TRANSFORMATION;
D O I
10.1016/j.jre.2024.03.010
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Rare-earth (RE) magnesium alloys have attracted lots of attention due to their excellent mechanical properties. In this work, the microstructure and mechanical properties of as-extruded 8.5Gd-4.5Y-0.8Zn-0.4Zr magnesium alloy under different solution treatment were examined with the optical microscope (OM), scanning electron microscope (SEM), high resolution transmission electron microscope (HRTEM), electron back-scattered diffraction (EBSD) and Instron testing machine. The results show that the ES12 alloy (solution treatment for 12 h at 520 degrees C) has the highest ultimate tensile strength (UTS) of 390 MPa with a fracture elongation of 24.5% at the cost of a minor drop in yielding strength (YS) compared to the as-extruded alloy. During solution treatment, the block-shaped long period stacking ordered (LPSO) in as-extruded alloy evolves into plate-shaped LPSO, which disperses at grain boundaries (GBs), and lamellar LPSO, which distributes in grains. The coexistence of plate-shaped and lamellar LPSO, which impedes the dislocations movement, and the activated <c + a> dislocations are regarded as the primary reasons for mechanical properties improvement. Furthermore, the (11-21) <1-100> texture in as-extruded alloy transforms into the (11-20) <0001> texture in ES12 alloy. The average grain size increases from 3.45 mu m in as-extruded alloy to 18.70 mu m in ES12 alloy. The Schmid factors of {0001} <11-20>, {10-10} <11-20>, {10-11} <11-20>, and {11-22} <11-23> increase, which indicate that slip systems are more easily activated in plastic deformation. The dynamic recrystallization (DRX) grains fraction increase to 92.8% for ES12 alloy due to the particle-stimulated nucleation (PSN) mechanism triggered by block-shaped and plate-shaped LPSO. The freshly DRXed grains further weaken the texture, and reduce the dislocation density. All of these factors increase elongation of RE magnesium alloy. (c) 2024 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights are reserved, including those for text and data mining, AI training, and similar technologies.
引用
收藏
页码:832 / 842
页数:11
相关论文
共 73 条
  • [1] Long-period ordered structure in a high-strength nanocrystalline Mg-1 at% Zn-2 at% Y alloy studied by atomic-resolution Z-contrast STEM
    Abe, E
    Kawamura, Y
    Hayashi, K
    Inoue, A
    [J]. ACTA MATERIALIA, 2002, 50 (15) : 3845 - 3857
  • [2] Tunable and wideband high-performance rare earth-doped Ni-Mg-Cu-Zn nano ferrite-based meta-absorbers for C-band application
    Akhtar, Majid Niaz
    Alelyani, Magbool
    Alzahrani, Fatimah Mohammed A.
    Almohammedi, Abdullah
    Qamar, Sabih
    Baqir, M. A.
    Irfan, M.
    Khan, Muhammad Azhar
    Albarkaty, Kheir S.
    Alrowaili, Z. A.
    Al-Buriahi, M. S.
    [J]. JOURNAL OF RARE EARTHS, 2025, 43 (01) : 124 - 132
  • [3] TENSILE-COMPRESSIVE YIELD ASYMMETRIES IN HIGH-STRENGTH WROUGHT MAGNESIUM ALLOYS
    BALL, EA
    PRANGNELL, PB
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (02): : 111 - 116
  • [4] The texture and anisotropy of magnesium-zinc-rare earth alloy sheets
    Bohlen, Jan
    Nuernberg, Marcus R.
    Senn, Jeremy W.
    Letzig, Dietmar
    Agnew, Sean R.
    [J]. ACTA MATERIALIA, 2007, 55 (06) : 2101 - 2112
  • [5] Effect of rare earth elements on the microstructure and texture development in magnesium-manganese alloys during extrusion
    Bohlen, Jan
    Yi, Sangbong
    Letzig, Dietmar
    Kainer, Karl Ulrich
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (26): : 7092 - 7098
  • [6] Weak strengthening effect of the precipitated lamellar phase in the homogenized Mg-8Gd-4Y-1.6Zn-0.5Zr (wt%) alloy followed by furnace cooling
    Chen, D. J.
    Zhang, K.
    Li, T.
    Li, X. G.
    Li, Y. J.
    Ma, M. L.
    Shi, G. L.
    Yuan, J. W.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 744 : 1 - 9
  • [7] Effect of Ti addition on the microstructure and mechanical properties of cast Mg-Gd-Y-Zn alloys
    Cheng, Peng
    Zhao, Yuhong
    Lu, Ruopeng
    Hou, Hua
    Bu, Zhiqiang
    Yan, Feng
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 708 : 482 - 491
  • [8] Novel equilibrium two phase Mg alloy with the long-period ordered structure
    Chino, Y
    Mabuchi, M
    Hagiwara, S
    Iwasaki, H
    Yamamoto, A
    Tsubakino, H
    [J]. SCRIPTA MATERIALIA, 2004, 51 (07) : 711 - 714
  • [9] Structure and stacking faults in layered Mg-Zn-Y alloys: A first-principles study
    Datta, Aditi
    Waghmare, U. V.
    Ramamurty, U.
    [J]. ACTA MATERIALIA, 2008, 56 (11) : 2531 - 2539
  • [10] The main strengthening phases transformation and their strengthening mechanisms in as-cast Mg-Gd-(Y)-Zn alloys: A review
    Deng, Daiyi
    Cheng, Renju
    Jiang, Bin
    Yang, Mingbo
    Wang, Haijun
    Zhou, Yongfeng
    Yu, Chuntang
    Ma, Yanlong
    Peng, Jian
    Pan, Fusheng
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 968