The Effect of Irradiation Dose and Temperature on Irradiation Hardening and Microstructure Study of Hot-Forged V-4Cr-4Ti Under Self-Ion Irradiation

被引：0

作者：

Wei, Yaxia ^{[1
]}

Zhao, Yinshu ^{[1
]}

Xu, Min ^{[1
]}

Zheng, Pengfei ^{[1
]}

Guo, Liping ^{[2
]}

Luo, Hongtai ^{[2
]}

Zhang, Pengbo ^{[3
]}

Zhang, Guihang ^{[1
]}

Zhao, Hua ^{[1
]}

机构：

[1] Southwestern Inst Phys, Chengdu 610041, Peoples R China

[2] Wuhan Univ, Sch Phys & Technol, Hubei Nucl Solid Phys Key Lab, Key Lab Artificial Micro & Nanostruct,Minist Educ, Wuhan 430072, Peoples R China

[3] Dalian Maritime Univ, Coll Sci, Dalian 116026, Peoples R China

来源：

METALS | 2025年 / 15卷 / 02期

基金：

中国国家自然科学基金;

关键词：

vanadium alloy; irradiation hardening; dislocation loops; self-ion irradiation; VANADIUM ALLOYS; FABRICATION; TECHNOLOGY;

D O I：

10.3390/met15020104

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

After being self-ion implanted at 400 degrees C and 550 degrees C, the microstructure and irradiation hardness of kilogram-scale V-4Cr-4Ti alloys were studied using a transmission electron microscope (TEM) and nano-indentation test technology. Irradiation was performed using self-ions (V2+) at 2.5 MeV with design influences of 1.15 x 1015 ions cm-2, 4.59 x 1015 ions cm-2, and 9.17 x 1015 ions cm-2, so that the peak damages of V-4Cr-4Ti alloys are 1, 4, and 8 dpa, respectively. Compared with the 400 degrees C samples, the 550 degrees C samples exhibited a higher-density number of dislocation loops and increased hardness and reached saturation at lower irradiation doses. The irradiation temperature was mainly responsible for these differences, and the potential mechanism for its effect on the irradiation behavior was discussed.

引用

页数：12

共 40 条

[21] Irradiation-induced precipitation in V-4Cr-4Ti alloys studied using three-dimensional atom probe
Hatakeyama, M.
Nagasaka, T.
Muroga, T.
Toyama, T.
Yamagata, I.
JOURNAL OF NUCLEAR MATERIALS, 2013, 442 (1-3) : S346 - S349
[22] Effect of Ti addition on microstructural evolution of V-Cr-Ti alloys to balance irradiation hardening with swelling suppression
Fukumoto, K.
Tone, K.
Onitsuka, T.
Ishigami, T.
NUCLEAR MATERIALS AND ENERGY, 2018, 15 : 122 - 127
[23] Microstructure evolution and hardening behavior in FCC Ni under ion irradiation: Influence of dose rate
Xia, Liang
Huang, Jia
Chen, Yiheng
Liu, Yuxin
Jin, Ke
Wang, Xujia
Xia, Shuan
Wang, Hongchang
Li, Ling
Xue, Jianming
Wang, Yugang
Wang, Chenxu
SCRIPTA MATERIALIA, 2025, 259
[24] A theoretical analytical model of temperature and irradiation dose dependent yield strength of metal materials under irradiation hardening effect
Dong, Pan
Ma, Yanli
Wei, Tianqi
Li, Ziyuan
Li, Weiguo
Ma, Jianzuo
JOURNAL OF NUCLEAR MATERIALS, 2024, 592
[25] The effect of final heat treatment temperature on radiation response of V-4Cr-4Ti
Muroga, T.
Nagasaka, T.
Watanabe, H.
Yamazaki, M.
JOURNAL OF NUCLEAR MATERIALS, 2011, 417 (1-3) : 310 - 313
[26] Abnormal hardening effect induced by the lath-like precipitates in the V-4Cr-4Ti alloy
Zhu, Boling
Yang, Shanwu
Ding, Jianwen
Zhang, Wenhua
Long, Yi
Wan, Farong
MATERIALS LETTERS, 2015, 161 : 609 - 612
[27] Effect of Carbon on Dislocation Loops Formation during Self-Ion Irradiation in Fe-Cr Alloys at High Temperatures
Shi, Tiantian
Liu, Wenbo
Su, Zhengxiong
Yan, Xu
Lu, Chenyang
Yun, Di
MATERIALS, 2022, 15 (06)
[28] Defect microstructure of a Ti64 alloy under TI2+ ion irradiation. Influence of dose and temperature
Doriot, Sylvie
Malaplate, Joel
Arnal, Benoit
Dalle, France
JOURNAL OF NUCLEAR MATERIALS, 2023, 583
[29] Microstructure evolution of cold-worked Zircaloy-4 under 20 mev Cu ion irradiation
Naceri, S. E.
Izerrouken, M.
Ishaq, A.
Guittoum, A.
Sari, A.
Khereddine, A.
Kadouma, M.
Menchi, O.
Ghamnia, M.
PHILOSOPHICAL MAGAZINE LETTERS, 2019, 99 (04) : 157 - 165
[30] Changes in the microstructure and mechanical properties of Ti-6Al-4V alloys induced by Fe ion irradiation at a high He generation rate
Jin, Peng
Shen, Tie-Long
Li, Jing
Yang, Yu-Shan
Liu, Chao
Cui, Ming-Huan
VACUUM, 2023, 207

← 1 2 3 4 →