The Effect of Irradiation Dose and Temperature on Irradiation Hardening and Microstructure Study of Hot-Forged V-4Cr-4Ti Under Self-Ion Irradiation

被引：0
|
作者：
Wei, Yaxia [1 ]
Zhao, Yinshu [1 ]
Xu, Min [1 ]
Zheng, Pengfei [1 ]
Guo, Liping [2 ]
Luo, Hongtai [2 ]
Zhang, Pengbo [3 ]
Zhang, Guihang [1 ]
Zhao, Hua [1 ]
机构：
[1] Southwestern Inst Phys, Chengdu 610041, Peoples R China
[2] Wuhan Univ, Sch Phys & Technol, Hubei Nucl Solid Phys Key Lab, Key Lab Artificial Micro & Nanostruct,Minist Educ, Wuhan 430072, Peoples R China
[3] Dalian Maritime Univ, Coll Sci, Dalian 116026, Peoples R China
来源：
METALS | 2025年 / 15卷 / 02期
基金：
中国国家自然科学基金;
关键词：
vanadium alloy; irradiation hardening; dislocation loops; self-ion irradiation; VANADIUM ALLOYS; FABRICATION; TECHNOLOGY;
D O I：
10.3390/met15020104
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
After being self-ion implanted at 400 degrees C and 550 degrees C, the microstructure and irradiation hardness of kilogram-scale V-4Cr-4Ti alloys were studied using a transmission electron microscope (TEM) and nano-indentation test technology. Irradiation was performed using self-ions (V2+) at 2.5 MeV with design influences of 1.15 x 1015 ions cm-2, 4.59 x 1015 ions cm-2, and 9.17 x 1015 ions cm-2, so that the peak damages of V-4Cr-4Ti alloys are 1, 4, and 8 dpa, respectively. Compared with the 400 degrees C samples, the 550 degrees C samples exhibited a higher-density number of dislocation loops and increased hardness and reached saturation at lower irradiation doses. The irradiation temperature was mainly responsible for these differences, and the potential mechanism for its effect on the irradiation behavior was discussed.
引用
收藏
页数：12
相关论文
共 40 条
  • [11] Microstructural changes and irradiation hardening behavior of V-4Cr-4Ti alloys irradiated with He ions using flash-electropolishing
    Fukumoto, Ken-ichi
    Zou, Yichen
    Nagasaka, Takuya
    Ishigami, Ryoya
    JOURNAL OF NUCLEAR MATERIALS, 2025, 603
  • [12] Microstructural changes of Y-doped V-4Cr-4Ti alloys after ion and neutron irradiation
    Watanabe, H.
    Yamasaki, K.
    Higashijima, A.
    Taguma, H.
    Nagasaka, T.
    Muroga, T.
    NUCLEAR MATERIALS AND ENERGY, 2016, 9 : 447 - 450
  • [13] Varying temperature irradiation effects of V-4Cr-4Ti alloy with small addition of Si, Al and Y
    Satou, M
    Nakayashiki, H
    Chuto, T
    Hasegawa, A
    Abe, K
    EFFECTS OF RADIATION ON MATERIALS: 21ST INTERNATIONAL SYMPOSIUM, 2004, 1447 : 714 - 724
  • [14] Deuterium permeation through the low-activated V-4Cr-4Ti alloy under plasma irradiation
    Cherkez, D., I
    Spitsyn, A., V
    Golubeva, A., V
    Chernov, V. M.
    NUCLEAR MATERIALS AND ENERGY, 2020, 23
  • [15] Effect of yttrium content on microstructure and irradiation behavior of V-4Cr-4Ti-xY alloys
    Luo, Hongtai
    Luo, Fengfeng
    Chen, Yiheng
    Wang, Jiawei
    Liu, Qiuxiang
    Li, Fang
    Xie, Ziyang
    Lin, Wenbin
    Guo, Liping
    JOURNAL OF NUCLEAR MATERIALS, 2022, 559
  • [16] Suppressed defect production and hardening in refractory high entropy alloys under ion irradiation at early stage: A comparative study between VTaTi, HfNbZrTi, and conventional V-4Cr-4Ti
    Zhu, Zhixi
    Chen, Shang
    Zhang, Qiuhong
    Li, Lei
    Zhao, Yuqing
    Guo, Xun
    Uglov, V. V.
    Jin, Ke
    Xue, Yunfei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2025, 235 : 1 - 11
  • [17] Monolayer-thick TiO precipitation in V-4Cr-4Ti alloy induced by proton irradiation
    Impagnatiello, A.
    Shubeita, S. M.
    Wady, P. T.
    Ipatova, I.
    Dawson, H.
    Barcellini, C.
    Jimenez-Melero, E.
    SCRIPTA MATERIALIA, 2017, 130 : 174 - 177
  • [18] Inhibition of Ti-rich precipitates and improvement of the irradiation resistance in V-4Cr-4Ti by adding La element
    Luo, Hongtai
    Luo, Fengfeng
    Zhang, Weiping
    Guo, Liping
    Lin, Wenbin
    Yin, Zepeng
    Cao, Junjie
    JOURNAL OF NUCLEAR MATERIALS, 2024, 591
  • [19] Effect of tellurium (Te4+) irradiation on microstructure and associated irradiation-induced hardening*
    Huang, Hefei
    Liu, Jizhao
    Lei, Guanhong
    Muransky, Ondrej
    Wei, Tao
    Ionescu, Mihail
    CHINESE PHYSICS B, 2021, 30 (05)
  • [20] Effects of irradiation temperature and dose rate on the mechanical properties of self-ion implanted Fe and Fe-Cr alloys
    Hardie, Christopher D.
    Williams, Ceri A.
    Xu, Shuo
    Roberts, Steve G.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 439 (1-3) : 33 - 40
1234