Precipitation Behavior of η Phase and Its Effect on Hot Deformation in 718Plus Alloy

被引：0

作者：

Kou, Jinfeng ^{[1
]}

Bai, Yaguan ^{[1
]}

Zhang, Xin ^{[1
]}

Guo, Wei ^{[1
]}

Zhang, Bingbing ^{[1
]}

Li, Hongmei ^{[1
]}

Nie, Yihong ^{[2
]}

机构：

[1] Tianjin Heavy Ind Res & Dev Co Ltd, Tianjin 300457, Peoples R China

[2] China First Heavy Ind, Qiqihar 161042, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2024年 / 53卷 / 12期

关键词：

718Plus alloy; i phase; precipitation; dissolution; dynamic recrystallization; MECHANICAL-PROPERTIES; ATI; 718PLUS; MICROSTRUCTURE;

D O I：

10.12442/j.issn.1002-185X.20230655

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Solid-state microstructure, microstructure evolution of i phase and the recrystallization microstructure of 718Plus alloy with different i phase after compression with different compression amounts were investigated by OM, SEM and the thermal simulation compression testing machine. The compression process of different temperatures and deformation rates were obtained. The results show that the peak temperature of i phase precipitation occurs at 900 degrees C. The dissolution behavior of i phase is mainly affected by solution time, and it dissolves effectively after solution treatment at 1040 degrees C for 2 h. A small quantity of i phase contributes to dynamic recrystallization in large deformation process while a large quantity of i phase restrain dynamic recrystallization. At appropriate deformation temperature and rate, a small quantity of i phase interacts with the dynamic recrystallization process, which makes for the uniform fine crystal structure.

引用

页码：3465 / 3474

页数：10

共 21 条

[1] Du Jinhui, Lv Xudong, Deng Qun, Et al., Materials China(中国材料进展), 31, 12, (2012)
[2] Asala G, Andersson J, Ojo O A., Philosophical Magazine, 99, 4, (2019)
[3] Shi Zhaoxia, Xu Guohua, Liu Ning, Et al., Rare Metal Materials and Engineering(稀有金属材料与工程), 52, 8, (2023)
[4] Wang Miaoquan, Tian Chengang, Nan Yang, Et al., Materials Reports(材料导报), 31, 10, (2017)
[5] Zhang J B, Li J A, Peng Y Y, Et al., Materials Transactions, 36, 4, pp. 20050167-3, (2022)
[6] Kattoura M, Viswanathan G B, Mannava S R, Et al., Metallurgical and Materials Transactions A, 52, (2021)
[7] Xie Xishan, Wang Gailian, Dong Jianxin, Loria E A., Superalloys 718, 625, 706 and Various Derivatives, (2005)
[8] Xie Xishan, Liang Qiang, Dong Jianxin, Loria E A., Superalloys 718, 625, 706 and Various Derivatives, (1994)
[9] Krakow R, Jonestone D N, Eggeman A S, Et al., Acta Materialia, 130, (2017)
[10] Hanning F, Khan A K, Andersson J, Et al., Welding in World, 64, (2020)

← 1 2 3 →