Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins

This study aimed to assess the impact of various fabrication techniques and polishing procedures on the surface roughness (Ra) of resin-based materials used in the fabrication of complete dentures. A total of 90 specimens were produced from resin, CAD-CAM milled PMMA resin, and 3D-printed resin (n = 30). Each specimen measured 10 mm in diameter and 2 mm in height. The surface roughness (Ra) values of the specimens were initially determined using a contact profilometer following fabrication. Subsequently, each group of specimens was polished with 600-, 800-, and 1000-grit silicon carbide abrasive papers under running water. A second measurement of the surface roughness (Ra) values was then performed. The data were analyzed statistically using the Kruskal-Wallis test, Mann-Whitney U test, Wilcoxon signed-rank test, and paired samples t-test (p = 0.05). A statistically significant difference was identified between the groups in terms of surface roughness (Ra) prior to the polishing process (p < 0.001). However, no statistically significant difference was observed between the milled and heat-polymerized PMMA base materials following the polishing process. The 3D-printed specimens showed the most notable improvement in surface roughness due to the polishing process. Nevertheless, their surface roughness remained statistically significantly higher compared to the other samples, both before after polishing.