Effect of Cr addition on the microstructure and properties of Cu-15Ni-8Sn alloy

被引：1

作者：

Yuan, Mingquan ^{[1
]}

Tang, Kun ^{[1
]}

Guo, Chengjun ^{[1
,2
]}

Chen, Jinshui ^{[1
]}

Shi, Yufan ^{[1
]}

Yang, Bin ^{[1
]}

机构：

[1] Jiangxi Univ Sci & Technol, Fac Mat Met & Chem, Ganzhou 341000, Peoples R China

[2] Ningbo Changzhen Copper Ind Co Ltd, Ningbo 315400, Peoples R China

来源：

MATERIALS TODAY COMMUNICATIONS | 2025年 / 44卷

基金：

中国国家自然科学基金;

关键词：

Cu-15Ni-8Sn alloy; Cr addition; Discontinuous precipitation; Microstructure and Properties;

D O I：

10.1016/j.mtcomm.2025.111874

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The Cu-15Ni-8Sn alloy has attracted considerable attention as a novel copper-based alloy material. The impact of chromium (Cr) addition on the microstructure and properties of the Cu-15Ni-8Sn alloy were investigated by using optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that the incorporation of Cr reduces the secondary dendrite spacing in as-cast alloys and effectively mitigates dendrite segregation. Additionally, Cr begins to precipitate during the solidification process, forming Cr-rich phases. During the aging process, these Cr phases occupy the nucleation sites of the discontinuous precipitates and impede the movement of their front interfaces, thereby effectively suppressing the formation of discontinuous precipitates. The addition of 0.7 wt% Cr exhibited the most pronounced inhibitory effect, leading to a peak hardness of 357.9 HV, tensile strength of 742.6 MPa, and conductivity of similar to 9.8 % IACS after aging at 450 degrees C for 7 hours.

引用

页数：9

共 37 条

[1] On the discontinuous precipitation reaction and solute redistribution in a Cu-15%Ni-8%Sn alloy [J].

Alili, B. ;

Bradai, D. ;

Zieba, P. .

MATERIALS CHARACTERIZATION, 2008, 59 (10) :1526-1530

[2] Effect of chromium content on precipitation in Cu-Cr-Zr alloys [J].

Bodyakova, Anna ;

Mishnev, Roman ;

Belyakov, Andrey ;

Kaibyshev, Rustam .

JOURNAL OF MATERIALS SCIENCE, 2022, 57 (27) :13043-13059

[3] High strength and excellent softening resistance Cu-15Ni-8Sn alloy by Ti addition [J].

Chen, Liangguo ;

Liang, Yuanxin ;

Luo, Boyi ;

Ding, Biao ;

Shen, Zhe ;

Zhang, Shunran ;

Lu, Haibiao ;

Zheng, Tianxiang ;

Li, Qiang ;

Zhou, Bangfei ;

Liu, Chunmei ;

Ren, Weili ;

Zhong, Yunbo .

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 30 :4552-4563

[4]

Chen Q.L., 2020, D. Jiangxi Univ. Sci. Technol., DOI [10.27176/d.cnki.gnfyc.2020.000140, DOI 10.27176/D.CNKI.GNFYC.2020.000140]

[5] Refinement effect of C addition on the Cr phase in the as-cast Cu-Cr alloys [J].

Chen, W. ;

Hu, X. N. ;

Zou, J. ;

Guo, W. ;

Lu, D. P. ;

Tan, D. Q. .

VACUUM, 2020, 179

[6] Spinodal copper alloy C72900-new high strength antifriction alloy system [J].

Cribb, W. R. ;

Grensing, F. C. .

CANADIAN METALLURGICAL QUARTERLY, 2011, 50 (03) :232-239

[7]

Cribb WR, 2013, ADV MATER PROCESS, V171, P20

[8]

Fang S.P., 2020, J. Foundry Technol., V4, P384, DOI [10.16410/j.issn10008365.2020.04.021, DOI 10.16410/J.ISSN10008365.2020.04.021]

[9] Effects of P addition on spinodal decomposition and discontinuous precipitation in Cu-15Ni-8Sn alloy [J].

Guo, Chengjun ;

Shi, Yufan ;

Chen, Jinshui ;

Xiao, Xiangpeng ;

Liu, Baixiong ;

Liu, Jinpin ;

Yang, Bin .

MATERIALS CHARACTERIZATION, 2021, 171

[10] Inhibition of discontinuous precipitation and enhanced properties of Cu-15Ni-8Sn alloy with Fe addition [J].

Guo, Chengjun ;

Wan, Jia ;

Chen, Jinshui ;

Xiao, Xiangpeng ;

Huang, Hao ;

Liu, Jinping ;

Yang, Bin .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 795

← 1 2 3 4 →