Effect of hot drawing on the properties of three-dimensional braided polylactic acid composites

被引：0

作者：

Wang, Jing ^{[1
,2
]}

Lu, Xiaonan ^{[1
,2
]}

Lyu, Dongyang ^{[1
,2
]}

Jiao, Yanan ^{[1
,2
]}

机构：

[1] School of Textile Science and Engineering, Tiangong University, Tianjin

[2] Ministry of Education, Key Laboratory of Advanced Textile Composite Materials, Institute of Composite Materials, Tiangong University, Tianjin

来源：

Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2025年 / 42卷 / 02期

关键词：

hot drawing; hot pressing; polylactic acid; thermoplastic composite; three-dimensional braiding;

D O I：

10.13801/j.cnki.fhclxb.20240430.004

中图分类号：

学科分类号：

摘要：

Three-dimensional braided thermoplastic composites are characterized by easier recycling and shorter production cycles. Among them, polylactic acid (PLA) has received wide attention for its better biocompatibility and lower cost. The hot pressing (HP) process has a high degree of design freedom, however, the adoption of the HP process for the preparation of three-dimensional braided PLA composites may destroy the braided structure due to the extrusion of the preform during mold closure, resulting in the uneven distribution of the fibers, destroying the interfacial properties, and leading to the degradation of the mechanical properties. As a self-reinforcing technology, hot drawing (HD) can effectively improve the crystallinity of PLA and the mechanical properties of composites by applying a tensile force in the axial direction of the three-dimensional braided preforms based on the HP process. In this experiment, the glass fiber (GF) reinforced PLA composites were prepared and tested by two molding processes, HD and HP, respectively, and it was found that: The shear strength of HD composites compared with HP composites was 33.03% higher, the bending strength was 26.92% higher, the tensile strength was 39.67% higher, and the degree of crystallinity was increased by 20.03%, and the thermal stability was slightly improved. The hot drawing process promoted the orderly arrangement of PLA molecular crystals along the axial direction and the growth of nuclei, which led to a simpler arrangement of PLA molecular chains and improved the crystallinity of PLA, as well as the mechanical properties of the composites. Combining macroscopic as well as 3D profile observation, it is found that the HD process improves the problem of damage to the braided structure, ensures the integrity of the three-dimensional braided knots, and arranges the GF fiber bundles in an orderly manner, which is conducive to the improvement of the overall performance of the composites. © 2025 Beijing University of Aeronautics and Astronautics (BUAA). All rights reserved.

引用

页码：773 / 781

页数：8

共 30 条

[1]

PUGLIA D, LUZI F, TORRE L., Preparation and applications of green thermoplastic and thermosetting nanocomposites based on nanolignin, Polymers, 14, 24, (2022)

[2]

CAMPOS B M, BOURBIGOT S, FONTAINE G, Et al., Thermoplastic matrix-based composites produced by resin transfer molding: A review, Polymer Composites, 43, 5, pp. 2485-2506, (2022)

[3]

ALSHAMMARI B A, ALSUHYBANI M S, ALMUSHAIKEH A M, Et al., Comprehensive review of the properties and modifications of carbon fiber-reinforced thermoplastic composites, Polymers, 13, 15, (2021)

[4]

ALMUSHAIKEH A M, ALASWAD S O, ALSUHYBANI M S, Et al., Manufacturing of carbon fiber reinforced thermoplastics and its recovery of carbon fiber: A review, Polymers Testing, 122, (2023)

[5]

AN W L, WANG X L, LIU X H, Et al., Chemical recovery of thermosetting unsaturated polyester resins, Green Chemistry, 24, 2, pp. 701-712, (2022)

[6]

KORKMAZ M, OKUR A., The review about the numerical modelling and analysis of 3D woven fabrics, Journal of the Textile Institute, 114, 3, pp. 496-522, (2022)

[7]

GRIES T, BETTERMANN I, BLAUROCK C, Et al., Aachen technology overview of 3D textile materials and recent innovation and applications, Applied Composite Materials, 29, 1, pp. 43-64, (2022)

[8]

LI Zilun, YANG Ankun, QIN Xiaohong, Et al., Temperature effect on axial compressive properties of three-dimensional glass fiber/epoxy resin braided composite thin-walled tubes, Acta Materiae Compositae Sinica, 40, 10, pp. 5588-5600, (2023)

[9]

GU Q J, QUAN Z Z, SHEN M D, Et al., Fabrication and braiding angle effect on the improved interlaminar shear performances of 3D braided sandwich hybrid composites, Journal of Materials Research and Technology, 25, pp. 5795-5806, (2023)

[10]

ZHANG D, ZHENG X T, WANG Z B, Et al., Effects of braiding architectures on damage resistance and damage tolerance behaviors of 3D braided composites, Composite Structures, 232, (2020)

← 1 2 3 →