Time-frequency analysis of acoustic emission signals in composite materials under repeated impact conditions

被引：0

作者：

Du, Jinbo ^{[1
,2
,3
,4
]}

Bao, Yunpeng ^{[1
]}

Wang, Weiwei ^{[5
]}

Cai, Qianyu ^{[2
]}

Wang, Han ^{[1
,2
]}

Cui, Jialin ^{[6
]}

Chronopoulos, Dimitrios ^{[3
,4
]}

Hu, Peijun ^{[1
]}

机构：

[1] Zhejiang Univ, Sch Mech Engn, State Key Lab Fluid Power & Mechatron Syst, Hangzhou 310027, Peoples R China

[2] Zhejiang Univ, Sch Mech Engn, Key Lab Adv Mfg Technol Zhejiang Prov, Hangzhou, Peoples R China

[3] Katholieke Univ Leuven, Dept Mech Engn, Leuven, Belgium

[4] Katholieke Univ Leuven, Div Mechatron Syst Dynam LMSD, Leuven, Belgium

[5] Shanghai Inst Satellite Engn, Mech Technol Lab, Shanghai, Peoples R China

[6] Harbin Engn Univ, Coll Shipbldg Engn, Harbin, Peoples R China

来源：

POLYMER COMPOSITES | 2025年

关键词：

acoustic emission; laminated composite; repeated impact; time-frequency analysis; wavelet packed transform; WAVELET TRANSFORM; DAMAGE; DELAMINATION; CLASSIFICATION; FAILURE;

D O I：

10.1002/pc.29752

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

In the service of composite materials, scenarios involving repeated impacts are frequently encountered. In our study, the time-frequency characteristics of acoustic emission signals during repeated impact processes were investigated using wavelet packet transform. Principal Component Analysis was utilized to identify the frequency bands containing the most information. Shannon entropy was employed to select the optimal wavelet basis function. The terms DDD3, ADD3, and DAA3 correspond to matrix cracking, delamination, and fiber failure, respectively. The initial impact, due to the presence of numerous internal voids in the specimen, often leads to stress concentration, thus resulting in a prolonged duration of matrix cracking during the initial impact. Delamination becomes more active when matrix cracking initially occurs. Fiber failure typically accompanies unloading when it becomes active. Matrix cracking dissipates the most energy, followed by delamination and then fiber failure. When the final impact penetration occurs, the characteristic frequency band proportions for the quasi-isotropic matrix cracking, delamination, and fiber failure are 48.99%, 22.39%, and 7.16%, respectively. For the cross-ply laminate, the corresponding proportions of the characteristic frequency bands are 56.62%, 14.46%, and 6.98%, respectively.

引用

页数：14

共 33 条

[21] Barile C., Casavola C., Pappalettera G., Vimalathithan P.K., Damage characterization in composite materials using acoustic emission signal-based and parameter-based data, Compos B Eng, 178, (2019)
[22] Ni Q.Q., Iwamoto M., Wavelet transform of acoustic emission signals in failure of model composites, Eng Fract Mech, 69, pp. 717-728, (2002)
[23] Karimi N.Z., Minak G., Kianfar P., Analysis of damage mechanisms in drilling of composite materials by acoustic emission, Compos Struct, 131, pp. 107-114, (2015)
[24] Heidary H., Karimi N.Z., Ahmadi M., Rahimi A., Zucchelli A., Clustering of acoustic emission signals collected during drilling process of composite materials using unsupervised classifiers, J Compos Mater, 49, pp. 559-571, (2015)
[25] Sakly A., Laksimi A., Kebir H., Benmedakhen S., Experimental and modelling study of low velocity impacts on composite sandwich structures for railway applications, Eng Fail Anal, 68, pp. 22-31, (2016)
[26] Katunin A., Pawlak S., Wronkowicz-Katunin A., Tutajewicz D., Damage progression in fibre reinforced polymer composites subjected to low-velocity repeated impact loading, Compos Struct, 252, (2020)
[27] Atas C., Dogan A., An experimental investigation on the repeated impact response of glass/epoxy composites subjected to thermal ageing, Compos B Eng, 75, pp. 127-134, (2015)
[28] Sevkat E., Liaw B., Delale F., Raju B.B., Effect of repeated impacts on the response of plain-woven hybrid composites, Compos B Eng, 41, pp. 403-413, (2010)
[29] Carvajal D.R.A., Correa R.A.M., Casas-Rodriguez J.P., Durability study of adhesive joints used in high-speed crafts manufactured with composite materials subjected to impact fatigue, Eng Fract Mech, 225, (2020)
[30] Xu D., Liu P.F., Chen Z.P., Damage mode identification and singular signal detection of composite wind turbine blade using acoustic emission, Compos Struct, 255, (2021)

← 1 2 3 4 →