Evolution mechanism of element Ni on matrix, surface and interface during static soaking of copper-nickel alloy

被引:2
作者
Gao, Zhixian [1 ,4 ]
Sun, Dandan [2 ]
Wu, Kaijin [3 ]
Dong, Caichang [2 ]
Zhang, Bo [2 ]
Gao, Rongjie [3 ]
Han, Bing [2 ]
Li, Xiangyang [4 ]
机构
[1] Cent Iron &Steel Res Inst Co Ltd, Beijing 100081, Peoples R China
[2] NCS Testing Technol Co Ltd, Beijing 100081, Peoples R China
[3] Ocean Univ China, Qingdao 266071, Peoples R China
[4] Cent Iron & Steel Res Inst, Beijing Adv Innovat Ctr Mat Genome Engn, Beijing 100081, Peoples R China
关键词
Copper-nickel alloy; XRF; XPS; EIS; Segregation; CU-NI; CORROSION BEHAVIOR; CHLORIDE; NACL; SEAWATER; FILM;
D O I
10.1016/j.surfin.2024.105224
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
This article uses XRF, WLI, SEM, EDS, XPS and EIS techniques to characterize the surface element segregation and the state of corrosion product films under different periods of artificial seawater immersion. The research results show that when the film is intact, a uniform Ni-rich layer is formed below the film due to the preferential dissolution of Cu elements, which weakens the segregation degree of Ni elements on the surface of the substrate. At the same time, Ni elements enter the film in the form of doping, which increases the resistance of the film. When the film layer is damaged, the Ni-rich layer between matrix and surface will be rapidly converted to NiO, the enrichment state of Ni element will be destroyed, and the segregation degree will be increased. However, NiO only plays a temporary protective role, and it is easy to hydrolysis into loose Ni (OH)2, resulting in the film layer fall off. After the matrix is exposed, the Cu element is preferentially dissolved again, and the nickel-rich layer is re-formed on the substrate surface.
引用
收藏
页数:12
相关论文
共 34 条
[1]  
[Anonymous], 2009, General Rules for Original Position Statistic Distribution Analysis Method National Steel Standardization Technical Committee
[2]  
BECCARIA AM, 1988, ANAL LETT, V21, P1433
[3]  
Cao C., 2002, An Introduction to Electrochemical Impedance Spectroscopy, V1
[4]   Corrosion of aluminium in the aqueous chemical environment of a loss-of-coolant accident at a nuclear power plant [J].
Chen, Dong ;
Howe, Kerry J. ;
Dallman, Jack ;
Letellier, Bruce C. .
CORROSION SCIENCE, 2008, 50 (04) :1046-1057
[5]   Corrosion behavior of copper-nickel alloys in neutral chloride and sulfide containing solutions [J].
Chervyakov, VN ;
Markos'yan, GN ;
Pchel'nikov, AP .
PROTECTION OF METALS, 2004, 40 (02) :111-115
[6]   CORROSION BEHAVIOR OF 70CU-30NI ALLOY IN 0.5M NACL AND IN SYNTHETIC SEAWATER [J].
DHAR, HP ;
WHITE, RE ;
DARBY, R ;
CORNWELL, LR ;
GRIFFIN, RB ;
BURNELL, G .
CORROSION, 1985, 41 (04) :193-196
[7]  
Dong C., 2023, Materials. (Basel), V16
[8]   Comparison of elemental resolved non-confined and restricted electrochemical degradation of nickel base alloys [J].
Dworschak, Dominik ;
Cheng, Hsiu-Wei ;
Ku, Ching-Shun ;
Chiang, Ching-Yu ;
Lin, Chia-Hsien ;
Valtiner, Markus .
CORROSION SCIENCE, 2021, 190
[9]   POTENTIAL-PH DIAGRAMS FOR 90-10 AND 70-30 CU-NI IN SEA-WATER [J].
EFIRD, KD .
CORROSION, 1975, 31 (03) :77-83
[10]   AC IMPEDANCE STUDY OF CU AND CU-NI ALLOYS IN AERATED SALT-WATER .1. PD COATING AND CORROSION PRODUCT STRIPPING [J].
HACK, HP ;
PICKERING, HW .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1991, 138 (03) :690-695