Novel Approach to Organization of Structured Cobalt-Based Fischer-Tropsch Catalyst

Structured Fischer-Tropsch synthesis catalysts were tested in tubular reactors of industry-standard diameters of 0.5 or 0.75 inches. The structured catalyst bed was manufactured by the obturation of a straight bunch of graphite-based extrudates (D = 1.5 mm, L = 30 mm). A conventional loose bed of granulated catalyst (D = 1.5 mm, L = 3 mm) was tested as a reference. In a 1000-3000 h-1 syngas space velocity range, structured and loose catalyst bed testing showed no significant differences in their main catalytic parameters. Nevertheless, their C5+ hydrocarbon group composition was quite different, i.e., the alkene fraction rose from 9 to 23%, while n-alkanes dropped from 81 to 64%. This could be a result of secondary reaction intensification in the conventional loose bed due to its zeolite acid site's higher availability. Further FTS testing of the structured catalysts in 4000-6000 h-1 manifested distinctive limits in C5+ productivity for 0.5 and 0.75 inches of 512 kg C5+/(m3 reactor<middle dot>h) and 362 kg C5+/(m3 reactor<middle dot>h), respectively. This may be explained by limitations in structured bed thermal conductivity. It suggests that the arrangement of extrudates in the structured catalyst can significantly affect the reaction heat and mass transfer conditions and affords new opportunities for group composition control by means of catalyst bed organization.