Surface modification of spring tine cultivator points with different metal powders by GTAW method

被引:0
作者
Can, K. [1 ]
Dalmis, I. S. [1 ]
机构
[1] Tekirdag Namik Kemal Univ, Mech Engng Dept, TR-59860 Corlu Tekirdag, Turkiye
关键词
Abrasive wear; Cultivator points; GTAW; Surface modification; Tillage tools; WEAR BEHAVIOR; MICROSTRUCTURE; STEEL; COATINGS; ALUMINUM; HARDNESS; IRON;
D O I
10.52292/j.laar.2024.1063
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The abrasive wear resistance of soil tillage tools is important for the agricultural equipment industry because abrasive wear caused by hard particles in the soil can shorten the lifespan of these parts. In this study, surface modification using FeCrC, FeTi, and Ni powders was carried out to improve the hardness and wear resistance of AISI 1040 material reversible spring tine cultivator points. The GTAW (Gas Tungsten Arc Welding) method was chosen for the energy input in the surface modification process due to its simplicity and efficiency. Microstructure studies were conducted using an optical microscope (OM), scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD). Additionally, microhardness measurements and wear tests were performed. It was found that the hardness values for all three coating types were higher than the ones measured in the substrate material. The maximum microhardness was 726.1 HV0.2 for the coating with a 70FeCrC + 30FeTi composition ratio. As a result of the increased hardness in the coating layer of the specimens, the wear resistance also increased. Abrasive wear tests were conducted under loads of 5 N, 10 N, and 15 N at distances of 400 m, 800 m, and 1200 m, respectively. The weight loss of the substrate was about 13 times higher compared to the coating containing 70FeCrC + 30FeTi. After the laboratory tests, cultivator points were coated and field tests were carried out.
引用
收藏
页码:45 / 53
页数:9
相关论文
共 38 条
  • [21] Wear of cultivator coulters reinforced with cemented-carbide plates and hardfacing
    Kostencki, Piotr
    Stawicki, Tomasz
    Krolicka, Aleksandra
    Sedlak, Pawel
    [J]. WEAR, 2019, 438
  • [22] Surface modification of AISI 4340 steel by multi-pass TIG arcing process
    Kumar, Sudhir
    Ghosh, P. K.
    Kumar, Ravindra
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2017, 249 : 394 - 406
  • [23] Microstructure and mechanical property of Ni-based thick coating remelted by gas tungsten arc
    Li Ya-long
    Dong Tian-shun
    Li Guo-lu
    Wang Hai-dou
    Fu Bin-Guo
    Zheng Xiao-dong
    Zhou Xiu-kai
    [J]. VACUUM, 2018, 155 : 260 - 269
  • [24] Microstructure of Cr3C2-reinforced surface metal matrix composite produced by gas tungsten arc melt injection
    Liu Aiguo
    Guo Mianhuan
    Hu Hailong
    Li Zhijie
    [J]. SCRIPTA MATERIALIA, 2008, 59 (02) : 231 - 234
  • [25] Protection of CK45 carbon steel tillage tools using TiN coating deposited by an arc-PVD method
    Malvajerdi, Shahab Sharifi
    Malvajerdi, Ahmad Sharifi
    Ghanaatshoar, Majid
    [J]. CERAMICS INTERNATIONAL, 2019, 45 (03) : 3816 - 3822
  • [26] Effect of surface modification on microstructure, hardness and wear rate of steels with 0.2%, 0.4% and 1.1 Wt%C by the addition of Titanium using Gas Tungsten Arc
    Mithun, C. M.
    Sellamuthu, R.
    Saravanan, R.
    [J]. MATERIALS TODAY-PROCEEDINGS, 2018, 5 (02) : 7586 - 7594
  • [27] Effect of Nickel content on hardness and wear rate of surface modified cast aluminum bronze alloy
    Nair, Sandeep
    Sellamuthu, R.
    Saravanan, R.
    [J]. MATERIALS TODAY-PROCEEDINGS, 2018, 5 (02) : 6617 - 6625
  • [28] Orhan A., 2008, PhD thesis
  • [29] Polat O., 2012, 3 UL TAS IM AN K BAL
  • [30] Sabet H, 2011, TRIBOL LETT, V44, P237, DOI 10.1007/s11249-011-9842-2