Properties and corrosion resistance mechanism of a self-healing octadecyl amine loaded ethyl cellulose microcapsule coatings loaded with epoxy resin

In order to provide long-term anti-corrosion properties of the coatings on the substrate, a microcapsule self-healing coatings system was designed in this paper. Microcapsules were synthesized with ethyl cellulose and octadecyl amine, which were added to epoxy resin to prepare self-healing coatings. The shape of microcapsules was spherical, the average particle size of microcapsules was about 100-120 mu m, and the average thickness of microcapsules was 4.43 mu m, which was conducive to the preparation of the coatings. The initial evaporation temperature of the microcapsules was 165 degrees C. The ethyl cellulose organic crosslinked shell enhances the strength of the microcapsules and improves the thermal stability of the microcapsules. Electrochemical impedance spectroscopy showed that the impedance of the coatings with 6 wt% microcapsules was about 2.68 x 106 Omega/cm2, which was 2 orders of magnitude higher than that of the coatings without microcapsules (5.23 x 104 Omega/cm2). Scanning electron microscope was used to observe the artificial scratches of the coatings for 24 h, and it was found that the microcapsule could repair the artificial scratches of the coatings well. The results showed that the addition of microcapsules can improve the anti-corrosion properties of the coatings.