Preparation and properties of CNTs/organic fluorine modified polyurethane-acrylate

被引：0
|
作者：
Chen, Jing [1 ]
Yang, Jianjun [1 ]
Wu, Qingyun [1 ]
Zhang, Jianan [1 ]
Wu, Mingyuan [1 ]
Liu, Jiuyi [1 ]
机构：
[1] Key Laboratory of Environment-friendly Polymer Materials of Anhui Province, School of Chemistry and Chemical Engineering, Anhui University, Hefei,Anhui,230601, China
来源：
Jingxi Huagong/Fine Chemicals | 2020年 / 37卷 / 01期
关键词：
Dopamine (DOA) and γ-aminopropyl triethoxysilane (APTES) were used to synergistically modify carbon nanotubes (CNTs) to prepare an A-DOA/CNTs material. The modified CNTs was grafted onto polyurethane containing double bond ends and copolymerized with 2-(perfluorooctyl) ethyl methacrylate (HDFDMA) and other ethylene monomers to prepare CNTs/organic fluorine modified polyurethane-acrylate (PUA) composite emulsions. The structure and properties of the materials were characterized and tested by FTIR; TEM; XPS; water contact angle measurement and tensile test. The results showed that when the mass fraction of A-DOA/CNTs was 0.75% and the mass fraction of HDFDMA was 12%; the 10% weight loss temperature of the film was 329℃; 37℃ higher than that of PUA film. The dynamic storage modulus (Eʹ) of composite film at -55℃ was the maximum; the glass transition temperature (Tg) was 79℃; the water absorption rate was 4.1%; the water contact angle was 110.8°; the tensile strength was 26.3 MPa; and the elongation at break was 352%. Compared with those of the unmodified film; the hydrophobicity; thermal stability and mechanical properties of the prepared film were significantly improved. © 2020; Editorial Office of FINE CHEMICALS. All right reserved;
D O I：
10.13550/j.jxhg.20190349
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：72 / 79
相关论文
共 50 条
  • [1] Preparation and Properties of Graphene Oxide-Modified Waterborne Polyurethane-Acrylate Hybrids
    Li, Pengling
    Ren, Hui
    Qiu, Fengxian
    Xu, Jicheng
    Yu, Zongping
    Yang, Pengfei
    Xu, Binbin
    Jiang, Yan
    Yang, Dongya
    POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2014, 53 (13) : 1408 - 1416
  • [2] Synthesis and Properties of Waterborne Polyurethane-acrylate Hybrid Emulsion Modified by Organic Silicane
    Lai, Xiaojuan
    Shen, Yiding
    Wang, Lei
    APPLICATIONS OF ENGINEERING MATERIALS, PTS 1-4, 2011, 287-290 : 1532 - 1537
  • [3] Preparation and Properties of Environmentally Friendly Waterborne Polyurethane-Acrylate
    Xu, Heping
    Qiu, Fengxian
    Wang, Yingying
    Wu, Wenling
    Chen, Zusheng
    Zhu, Junhua
    Yang, Dongya
    2011 INTERNATIONAL CONFERENCE ON MACHINE INTELLIGENCE (ICMI 2011), PT 2, 2011, 4 : 126 - 130
  • [4] Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane-acrylate composite
    Xu, Heping
    Qiu, Fengxian
    Wang, Yingying
    Yang, Dongya
    Wu, Wenling
    Chen, Zusheng
    Zhu, Junhua
    JOURNAL OF APPLIED POLYMER SCIENCE, 2012, 124 (02) : 958 - 968
  • [5] Preparation and application of perfluorinated polyurethane-acrylate
    Li, Pei-Zhi
    Shen, Yi-Ding
    Li, Gang-Hui
    Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2010, 26 (03): : 119 - 122
  • [6] Preparation, Characterisation and Mechanical Properties of Environmentally Friendly Waterborne Polyurethane and Polyurethane-Acrylate
    Qiu, Fengxian
    Zhang, Jingli
    Wu, Dongmei
    Zhang, Qinqin
    Yang, Dongya
    POLYMERS & POLYMER COMPOSITES, 2009, 17 (08): : 521 - 527
  • [7] Preparation and properties of surface modified GO modified amine-free waterborne polyurethane-acrylate emulsion
    Lai, Xiaojuan
    Zhang, Yinyin
    Liu, Jiahui
    Wang, Lei
    Huagong Jinzhan/Chemical Industry and Engineering Progress, 2020, 39 (04): : 1389 - 1395
  • [8] Preparation And Characterization Of Waterborne Polyurethane-acrylate Modified By Functionalized Graphene Oxide
    Lai, Xiaojuan
    Liu, Xiaohu
    Wang, Lei
    Yuan, Bin
    Liu, Guiru
    Cao, Hui
    JOURNAL OF APPLIED SCIENCE AND ENGINEERING, 2022, 26 (06): : 759 - 769
  • [9] Waterborne Polyurethane-Acrylate Containing Different Polyether Polyols: Preparation and Properties
    Xu, Heping
    Yang, Dongya
    Guo, Qing
    Wang, Yingying
    Wu, Wenling
    Qiu, Fengxian
    POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2012, 51 (01) : 50 - 57
  • [10] Preparation and properties of a novel waterborne fluorinated polyurethane-acrylate hybrid emulsion
    Wang, Chen
    Li, Xiaorui
    Du, Biao
    Li, Peizhi
    Lai, Xiaojuan
    Niu, Yuhua
    COLLOID AND POLYMER SCIENCE, 2014, 292 (03) : 579 - 587
12345