Structure and Mechanical Performance of 03Kh17N10M2 Steel Alloyed with Silver

被引：0

作者：

Kaplan, M.A. ^{[1
]}

Gorbenko, A.D. ^{[1
,2
]}

Ivannikov, A. Yu. ^{[1
]}

Mikhailova, A.V. ^{[1
]}

Konushkin, S.V. ^{[1
]}

Baikin, A.S. ^{[1
]}

Sergienko, K.V. ^{[1
]}

Morozova, Ya. A. ^{[1
,2
]}

Nasakina, E.O. ^{[1
]}

Kolmakov, A.G. ^{[1
]}

Sevostyanov, M.A. ^{[1
,2
]}

机构：

[1] Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences, Moscow,119934, Russia

[2] All-Russian Research Institute of Phytopathology, Moscow oblast, Bolshie Vyazemy,143050, Russia

来源：

Russian Metallurgy (Metally) | 2024年 / 2024卷 / 02期

关键词：

Manganese alloys - Remelting - Silver metallurgy;

D O I：

10.1134/S003602952470068X

中图分类号：

学科分类号：

摘要：

Abstract: The influence of silver additives in an amount of 0.2 and 0.5 wt % on the structure and mechanical properties of 03Kh17N10M2 steel sheets 1 μm thick has been studied. The steel has been obtained by means of argon arc remelting followed by homogenization annealing and hot longitudinal rolling. It has been found that when the silver content rises from 0 to 0.5 wt %, the strength parameters of the steel somewhat decline: σ0.2 and σr drop from 560 to 510 MPa and from 760 to 710 MPa, respectively, and the microhardness decreases from 274 to 250 HV. However, these values remain within the ASTM A240 requirements. In both cases, the fracture surface represents an ensemble of self-similar tough fracture pores (cups). The new type of steel (with a silver content of up to 0.5 wt %) may be efficient in the production of products with pronounced antibacterial properties. © Pleiades Publishing, Ltd. 2024.

引用

页码：374 / 378

页数：4

共 50 条

[1] STRUCTURE, TEXTURE AND STRENGTHENING OF HYDROPRESSED 03KH11N10M2T STEEL
ZVIGINTSEV, NV
YUSHKOV, VI
KHADYYEV, MS
KONAKOVA, IP
EFROS, BM
FIZIKA METALLOV I METALLOVEDENIE, 1986, 61 (06): : 1178 - 1183
[2] REFINING OF STRUCTURE OF MARAGING STEELS 03KH11N10M2T AND 03KH11N10M2TK6
FOKINA, AE
SMIRNOV, LV
SADOVSKII, VD
METAL SCIENCE AND HEAT TREATMENT, 1974, 16 (9-10) : 849 - 851
[3] STRUCTURE, TEXTURE AND STRENGTHENING OF PRESS FORGED STEEL 03Kh11N10M2T.
Zvigintsev, V.N.
Yushkov, V.I.
Khadyyev, M.S.
Konakova, I.P.
Efros, B.M.
Physics of Metals and Metallography, 1986, 61 (06): : 135 - 140
[4] STRUCTURE AND PROPERTIES OF WELD JOINTS OF 03KH11N10M2T1 STEEL
KRASNIKOVA, SI
PAUTKIN, VS
KUZMENKO, SI
DROBOT, AV
LISNICHENKO, LN
METAL SCIENCE AND HEAT TREATMENT, 1983, 25 (11-1) : 924 - 927
[5] Examination of the properties of forgings of 03Kh17N14M3 steel
Nikitaev, M.N.
Belinkii, A.L.
Zheltova, G.A.
Chemical and Petroleum Engineering, 1988, 24 (11-12) : 624 - 625
[6] Structure of 03KH14N10K5M2YU2T steel after laser treatment
Yu. R. Nemirovskii
M. S. Khadyev
L. A. Mal’tseva
T. V. Mal’tseva
A. L. Osintseva
Metal Science and Heat Treatment, 2009, 51
[7] Structure of 03KH14N10K5M2YU2T steel after laser treatment
Nemirovskii, Yu. R.
Khadyev, M. S.
Mal'tseva, L. A.
Mal'tseva, T. V.
Osintseva, A. L.
METAL SCIENCE AND HEAT TREATMENT, 2009, 51 (5-6) : 297 - 300
[8] PHYSICOMECHANICAL PROPERTIES AND STRUCTURE OF 03KH11N10M2T MARAGING-STEEL AFTER AGING
MIRONENKO, PA
MANKO, TA
KRASNIKOVA, SI
PILIPENKO, SP
STEEL IN THE USSR, 1985, 15 (12): : 606 - 608
[9] PHYSICOMECHANICAL PROPERTIES AND STRUCTURE OF 03Kh11N10M2T MARAGING STEEL AFTER AGING.
Mironenko, P.A.
Man'ko, T.A.
Krasnikova, S.I.
Pilipenko, S.P.
1600, (15):
[10] Structural transformations in steel 03Kh11N10M2T in dynamic aging
V. R. Vasil'ev
Yu. A. Kaplun
A. G. Rakhshtadt
Metal Science and Heat Treatment, 1998, 40 : 391 - 393

← 1 2 3 4 5 →