Effect of Temperature on Corrosion of Pipeline Steel in SRB/CO2 Environment

被引:0
作者
Pei, Wenxia [1 ]
Zhao, Guoxian [1 ]
Ding, Langyong [1 ]
Fang, Kun [1 ]
Wang, Fan [1 ]
Liu, Ranran [1 ]
机构
[1] School of Materials Science and Engineering, Xi’an Shiyou University, Xi’an
来源
Cailiao Daobao/Materials Reports | 2024年 / 38卷 / 23期
关键词
biofilm; microbial corrosion; pitting; sulfate-reducing bacteria; temperature;
D O I
10.11896/cldb.23070058
中图分类号
学科分类号
摘要
The present work explored the effect of temperature on its corrosion performance, and investigated the corrosion characteristics of X65 pipeline steel in sulfate reducing bacteria (SRB)/ saturated CO2 environment. Immersion and electrochemical tests were conducted on X65 pipeline steel at three temperature levels of 20 ℃, 40 ℃, and 60 ℃. The changes in SRB in the solution at high temperature were detected through 16S rRNA gene sequencing, and the surface morphology and pitting characteristics after corrosion were observed. The results showed that as temperature of the solution increased, SRB metabolism accelerated. Thermophilic SRB preferentially proliferated at high temperatures, and together with other thermophilic bacteria that produce S2-, it accelerated the generation of S2-, promoting the transition of S from an oxidizing state to a reducing state, and depositing it in corrosion products. At 40 ℃, the number of SRBs was the highest and the pitting rate was the highest, which could be attributed to the adsorption of SRBs on the surface of the sample. In the adsorption area of the SRB community, the reduction effect on the sample surface was enhanced, local cathodic reactions were accelerated too, and corrosion pores were generated. At 60 ℃, the uniform corrosion rate was the highest, the ion mass transfer was accelerated, and the thermophilic SRB genus largely proliferated. The combined action of microorganisms and CO2 caused severe uniform corrosion. © 2024 Cailiao Daobaoshe/ Materials Review. All rights reserved.
引用
收藏
相关论文
共 50 条
[21]   Effect of environmental factors on corrosion behaviour of L360QCS pipeline steel in H2S/CO2 environments [J].
Huang, X. S. ;
Qi, Y. M. ;
Chen, C. F. ;
Yu, H. B. ;
Lu, G. W. .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2015, 50 (03) :169-177
[22]   Modeling and experimental study of CO2 corrosion on carbon steel at elevated pressure and temperature [J].
Elgaddafi, Rida ;
Naidu, Adarsh ;
Ahmed, Ramadan ;
Shah, Subhash ;
Hassani, Shokrollah ;
Osisanya, Samuel O. ;
Saasen, Arild .
JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING, 2015, 27 :1620-1629
[23]   The Influence of O2 on the Corrosion Behavior of the X80 Steel in CO2 Environment [J].
Wang, Xiao ;
Wang, Xinyue ;
Wang, Jun ;
Wang, Guowei ;
Pan, Yi ;
Yan, Shuangchun .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01) :889-898
[24]   Influence of Cr content on corrosion performance of middle Cr alloy steel in CO2 environment [J].
Gu, Yang ;
Wu, Hui-bin ;
Yuan, Rui ;
Wang, Xin-tian ;
Wu, Tao ;
Shuai, Song .
MATERIALS RESEARCH EXPRESS, 2019, 6 (04)
[25]   Influence of microstructure on mechanical properties and corrosion behavior of 3%Cr steel in CO2 environment [J].
Xu, L. N. ;
Guo, S. Q. ;
Gao, C. L. ;
Chang, W. ;
Chen, T. H. ;
Lu, M. X. .
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2012, 63 (11) :997-1003
[26]   SRB Corrosion Behavior of L245 Pipeline Steel with Different Cathode Polarization Potential [J].
Li X. ;
Shang D.-Z. ;
Li Z.-M. ;
Jiang Y.-W. ;
Chen C.-F. .
Surface Technology, 2022, 51 (07) :207-217
[27]   Effects of Second Thermal Cycles on Microstructure and CO2 Corrosion Behavior of X80 Pipeline Steel [J].
Shi Chuanwei ;
Zhang Yuanbin ;
Liu Peng ;
Xie Yueliang .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2018, 13 (03) :2412-2429
[28]   Effects of temperature on the corrosion behavior of 13Cr martensitic stainless steel during exposure to CO2 and Cl- environment [J].
Zhang, H ;
Zhao, YL ;
Jiang, ZD .
MATERIALS LETTERS, 2005, 59 (27) :3370-3374
[29]   Study on corrosion behavior of L245 pipeline steel and joints in sulfate reducing bacteria environment [J].
Li X. ;
Li Z.-M. ;
Shang D.-Z. ;
Yu H.-B. ;
Chen C.-F. .
Surface Technology, 2021, 50 (03) :356-365
[30]   The effect of temperature, CO2, H2S gases and the resultant iron carbonate and iron sulfide compounds on the sour corrosion behaviour of ASTM A-106 steel for pipeline transportation [J].
Asadian, M. ;
Sabzi, M. ;
Anijdan, S. H. Mousavi .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2019, 171 :184-193