Synthesis and Performance Evaluation of Metallocene Polyalphaolefins (mPAO) Base Oil with Anti-Friction and Anti-Wear Properties

Anti-wear and anti-oxidation abilities are two key properties of lubricants that play a crucial role in ensuring long-term stable equipment operation. In this study, we aimed to develop a base oil with good anti-oxidation and anti-wear properties for use under extreme pressure. The as-prepared metallocene polyalphaolefin (mPAO) was chemically modified using the trifluoromethanesulfonic acid (TfOH) catalysis through an alkylating reaction with triphenyl phosphorothioate (TPPT). During the experiments, when the reaction temperature exceeded 70 degrees C or the concentration of TfOH exceeded 2.67%, the beta-scission reaction in the alkylation process became significantly more pronounced. The physical and chemical properties of TPPT-modified mPAO (T-mPAO) were evaluated by nuclear magnetic resonance spectroscopy, Fourier trans-form infrared spectroscopy, gel-permeation chromatography, and ASTM standards. T-mPAO showed significantly improved antioxidant capacity, with the initial oxidation temperature increasing by 32 degrees C compared to the base oil, and it exhibited the slowest increase in acid number in the 96-h oven oxidation test. The tribological tests showed that T-mPAO had the lowest friction coefficient, wear track, and wear rate (72.7% lower than that of mPAO) as well as the highest PB (238 kg) and PD (250 kg) among all tested samples. Compared to mPAO, the average friction coefficient of TPPT-modified mPAO in the four-ball friction test was reduced by 30.5%, and by 16.4% in the TE77 reciprocating friction test. Based on the experimental results, T-mPAO had strong anti-oxidation ability and excellent lubricating performance.The successful synthesis of multifunctional mPAO has enabled lubricant base oil additization, making it possible to use it in more demanding work scenarios, greatly broadening its application scope and making lubricant formulation blending more flexible.