An experimental calculation method for stress intensity factors of three-dimensional surface cracks

被引：0

作者：

Qi, Cong ^{[1
]}

Pi, Ai-guo ^{[1
]}

机构：

[1] Beijing Inst Technol, State Key Lab Explos Sci & Safety Protect, Beijing, Peoples R China

来源：

JOURNAL OF MECHANICS | 2024年 / 40卷

关键词：

reactive powder concrete; stress intensity factor; three-dimensional surface crack; 3D digital image correlation; REACTIVE POWDER CONCRETE; OPENING DISPLACEMENT;

D O I：

10.1093/jom/ufae058

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

Stress intensity factors (SIFs) are important parameters for evaluating structural reliability. This work combines CT in situ uniaxial compression experiment to study the main crack propagation trajectories of the reactive powder concrete (RPC) specimens. The three-dimensional ( 3D) displacement fields of RPC specimens with 3D surface cracks were analyzed using a 3D digital image correlation (3D-DIC) method. The 3D-DIC method was used to calculate the 3D surface crack SIFs of RPC specimens at different inclination angles, and the influence of crack inclination angles on SIFs was analyzed. The study found that the distribution pattern of SIFs calculated by the 3D-DIC method is consistent with the results obtained by the numerical method.

引用

页码：654 / 664

页数：11

共 50 条

[1] Rapid method of stress intensity factor calculation for semi-elliptical surface breaking cracks under three-dimensional contact loading
Fletcher, D. I.
Kapoor, A.
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART F-JOURNAL OF RAIL AND RAPID TRANSIT, 2006, 220 (03) : 219 - 234
[2] Stress intensity factors for surface cracks in single-edge notch bend specimen by a three-dimensional weight function method
Zhao, X. C.
Wu, X. R.
Newman, J. C.
Tong, D. H.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (11) : 1407 - 1418
[3] Characteristic-tensor method for efficient estimation of stress-intensity factors of three-dimensional cracks
Saito, Kei
Hirashima, Tei
Ma, Ninshu
Murakawa, Hidekazu
ENGINEERING FRACTURE MECHANICS, 2021, 257 (257)
[4] Three-dimensional weight function analyses and stress intensity factors for two unsymmetric surface cracks and surface-corner cracks at a circular hole
Zhang, Bo
Xu, Wu
Wu, Xue-Ren
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2022, 122
[5] Stress intensity formulas for three-dimensional cracks in the vicinity of an interface
Noda, Nao-Aki
Liang, Bin
JOURNAL OF TESTING AND EVALUATION, 2007, 35 (02) : 192 - 202
[6] Three-dimensional weight function analyses and stress intensity factors for two eccentric and asymmetric surface cracks and surface-corner cracks at a circular hole
Xu, Wu
Zhang, Bo
Wu, Xue-Ren
ENGINEERING FRACTURE MECHANICS, 2023, 277
[7] Stress intensity factors for three-dimensional weld toe cracks using weld toe magnification factors
Han, J. W.
Han, D. K.
Han, S. H.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2014, 37 (02) : 146 - 156
[8] Simulating three-dimensional stress intensity factors by the least-squares method
Ju, SH
INTERNATIONAL JOURNAL FOR NUMERICAL METHODS IN ENGINEERING, 1998, 43 (08) : 1437 - 1451
[9] Three-Dimensional Mixed Mode Stress Intensity Factors for Inclined Elliptical Surface Cracks in Plates under Uniform Tensile Load
Sahin, Hakan
Ayhan, Ali O.
1ST INTERNATIONAL WORKSHOP ON PLASTICITY, DAMAGE AND FRACTURE OF ENGINEERING MATERIALS (IWPDF 2019), 2019, 21 : 38 - 45
[10] The calculation of stress intensity factors by the surface integral method
Jin, CS
Jang, HS
Choi, HT
STRUCTURAL ENGINEERING AND MECHANICS, 1995, 3 (06) : 541 - 553

← 1 2 3 4 5 →