Synthesis of rice husk derived porous carbon as low-cost and high-performance electrode material for supercapacitors

Porous carbon electrode materials derived from agricultural by-products of food processing have attracted widespread interest. Rice husk (RH) is a promising raw material owing to its abundance and low price. In this study, a supercapacitor electrode was prepared by using recycled RH and secondarily activated with ZnCl2 to enhance its electrochemical energy storage performance. RH carbonized at the optimum temperature (i.e., 800 degrees C) was activated to synthesize RH-800-X (X = 1, 2, 3, 4, or 5, representing the mass ratio of ZnCl2 to RH-800). Sample RH-800-3 exhibited the highest specific surface area (1348.29 m(2) g(-1)) and mesoporous pore volume (0.8375 cm(3) g(-1)) among the samples. In a three-electrode system, the prepared electrodes delivered a high specific capacitance (242 F g(-1) at 0.3 A g(-1) in 6 M KOH solution). Furthermore, the capacitance retention of RH-800-3 remained at 99.9 % after 17,000 charge/discharge cycles. The results demonstrate the excellent capacitive behavior and superior electrochemical performance of RH-800-3. In addition, symmetrical capacitors prepared using RH-800-3 have an energy density of up to 101 Wh kg(-1) at a power density of 900 W kg(-1). Therefore, this study presents a simple and effective method for preparing a high-performance electrode material from biomass-derived porous carbon (i.e., recycled RH) and offers a new perspective for the efficient utilization of waste biomass resources.