The Effects of Metakaolin on the Properties of Magnesium Sulphoaluminate Cement

Magnesium sulphoaluminate (MSA) cement has good bonding properties and is suitable as an inorganic adhesive for repairing materials in civil engineering. However, there are still some problems with its use, such as its insufficient 1 day (d) strength and poor volumetric stability. This paper aims to investigate the influences of metakaolin (MK) on the physical and mechanical properties of magnesium sulphoaluminate (MSA) cement. The hydration products and microstructures of typical MSA cement samples were also analysed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS). The results showed that the addition of metakaolin reduces the fluidity and shortens the setting time of the MSA cement. The initial setting time and final setting time shortened maximally by 15-27 min and 25-48 min, respectively, with the addition of 10-30% metakaolin. Moreover, the compressive strength and flexural strength of the MSA cement improved significantly with the addition of 10-30% metakaolin at a curing age of 1 d. Compared with the compressive and flexural strengths of the control sample at 1 d, the compressive strengths of the modified samples showed obvious increases of 98%, 101%, and 109%, and the flexural strengths increased by 39%, 31%, and 26%, respectively, although they decreased slightly when the curing ages were 7 d, 14 d, and 28 d. The addition of 10% metakaolin improved the water resistance of the MSA cement immersed in water for 7 d and resulted in even higher water resistance at 28 d. The addition of 10-30% metakaolin improved the volumetric stability of the MSA cement with increasing dosages before 28 d of ageing. XRD and SEM-EDS analyses showed that the metakaolin accelerated the early hydration reaction and optimised the phase composition of the MSA cement. The results indicate that the addition of 10-20% metakaolin improved the strength after 1 d of ageing, water resistance, and volumetric stability of the MSA cement, providing theoretical support for the application of MAS cement as an inorganic bonding agent for repairing materials.