Investigations into Transgranular and Intergranular Stress Corrosion Cracking of Austenitic Stainless Steels in Hot Magnesium Chloride Solutions.

被引：0

作者：

Kessler, K.J. ^{[1
]}

Kaesche, H. ^{[1
]}

机构：

[1] Kraftwerkunion Erlangen, Erlangen, West Ger, Kraftwerkunion Erlangen, Erlangen, West Ger

来源：

Werkstoffe und Korrosion | 1984年 / 35卷 / 05期

关键词：

STAINLESS STEEL - Corrosion Protection;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The stress corrosion cracking (SCC) of austenitic stainless steels in hot magnesium chloride solutions is known to be transgranular. Therefore the slip-step-dissolution model is most favorable when explaining the failure mechanism. Constant load and constant extension rate tests (CERT) show that both methods are almost equivalent. Moreover constant extension rate tests in more concentrated magnesium chloride solutions at 135 degree C reveal a small potential range of intergranular stress corrosion cracking more negative than the range of transgranular SCC.

引用

页码：171 / 178

共 50 条

[1] INVESTIGATIONS INTO TRANSGRANULAR AND INTERGRANULAR STRESS-CORROSION CRACKING OF AUSTENITIC STAINLESS-STEELS IN HOT MAGNESIUM-CHLORIDE SOLUTIONS
KESSLER, KJ
KAESCHE, H
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1984, 35 (05): : 171 - 178
[2] STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS IN VARIOUS CHLORIDE SOLUTIONS.
Kowaka, Masamichi
Kudo, Takeo
Boshoku Gijutsu/Corrosion Engineering, 1976, 25 (09): : 551 - 559
[3] A CONTRIBUTION TO EXAMINATION OF STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS IN MAGNESIUM CHLORIDE SOLUTIONS
KOHL, H
CORROSION, 1967, 23 (02) : 39 - &
[4] STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS IN CHLORIDE SOLUTIONS
SHIMOSE, T
TAKAMURA, A
MORI, K
SHIMOGOR.K
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1965, 6 (02): : 83 - &
[5] The stress corrosion cracking behavior of austenitic stainless steels in boiling magnesium chloride solutions
Alyousif, Osama M.
Nishimura, Rokuro
CORROSION SCIENCE, 2007, 49 (07) : 3040 - 3051
[6] Effects of stress and temperature on stress corrosion cracking of austenitic stainless steels in concentrated magnesium chloride solutions
Jiang, XC
Staehle, RW
CORROSION, 1997, 53 (06) : 448 - 466
[7] CONSIDERATION OF THE TESTING METHODS OF THE SUSCEPTIBILITY TO STRESS CORROSION CRACKING FOR AUSTENITIC STAINLESS STEELS IN CONCENTRATED CHLORIDE SOLUTIONS.
Yamanaka, Kazuo
Kowaka, Masamichi
Sumitomo Metals, 1982, 34 (04): : 1 - 15
[8] Behaviour of Stress Corrosion Cracking of Austenitic Stainless Steels in Sodium Chloride Solutions
Elsariti, Samir Milad
Haftirman
MALAYSIAN TECHNICAL UNIVERSITIES CONFERENCE ON ENGINEERING & TECHNOLOGY 2012 (MUCET 2012), 2013, 53 : 650 - 654
[9] Stress corrosion cracking and hydrogen embrittlement of sensitized austenitic stainless steels in boiling saturated magnesium chloride solutions
Alyousif, Osama M.
Nishimura, Rokuro
CORROSION SCIENCE, 2008, 50 (08) : 2353 - 2359
[10] MECHANISM OF CHLORIDE STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS
RHODES, PR
CORROSION, 1969, 25 (11) : 462 - &

← 1 2 3 4 5 →