Development of residual stress measurement apparatus by neutron diffraction and its application to bent carbon steel

被引：5

作者：

Hayashi, Makoto ^{[1
]}

Ohkido, Shinobu ^{[2
]}

Minakawa, Nobuaki ^{[3
]}

Morii, Yukio ^{[3
]}

机构：

[1] Mech. Eng. Res. Lab., Hitachi Ltd., Kandatsu, Tsuchiura, 300-0013, Japan

[2] Mech. Eng. Res. Lab., Hitachi Ltd., Saiwaicho, Hitachi, 317-8511, Japan

[3] Tokai Res. Establishment, JAERI, Tokai, Ibaraki, 319-1106, Japan

来源：

Zairyo/Journal of the Society of Materials Science, Japan | 1998年 / 47卷 / 04期

关键词：

Mechanical variables measurement - Neutron diffraction - Plastic deformation - Plasticity - Residual stresses - Stress concentration - Tensile properties;

D O I：

10.2472/jsms.47.420

中图分类号：

学科分类号：

摘要：

To establish the measuring technique of neutron diffraction for the internal residual stress distribution in a structural component, a neutron diffraction apparatus was designed and manufactured in Modified Japan Research Reactor 3 (JRR3M). At the first step of measurement, a basic characteristics the diffractometer was evaluated. The incident neutron beam flux was 104n/cm2 sec and the Full Width at Half Maximum (FWHM) was about 0.3 degree. This indicates that the manufactured neutron diffractometer is capable for the residual stress measurement. As the first application of the neutron diffraction measurement, the residual stress distribution in plastically bent carbon steel plate was measured. A typical compressive-tensile-compressive-tensile residual stress pattern in the tangential direction in the bent plane was confirmed. The maximum stress near the surface was about 180 MPa. This means that the technique for residual stress measurement by neutron diffraction can be established in Japan.

引用

页码：420 / 426