CASTINGS IN VERY-LOW-CARBON CORROSION-RESISTING STEELS.

被引：0
|
作者：
Sadovnik, Yu.V.
Ushenin, I.M.
Pilipenko, V.N.
Pedorich, V.I.
机构：
来源：
Soviet Castings Technology (English Translation of Liteinoe Proizvodstvo) | 1987年 / 04期
关键词：
IRON AND STEEL METALLOGRAPHY - Microstructures - STEEL CASTINGS - Mechanical Properties - STEEL CORROSION - STEEL HEAT TREATMENT;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
To maximize the corrosion resistance of Cr-Ni steel components, their carbon content must be brought to within the solubility limit at temperatures at which structural and phase changes appear. For the majority of steels, this limit is below 0. 03% C. The authors investigated a melt containing 1. 94-2. 1% C, 17. 3-20. 3 Cr, 6. 2-9. 7% Ni, 0. 12-0. 25 Si, and 0. 027-0. 032% S. The carbon content is brought down from its original level to 0. 15-0. 25% by oxygen blowing, and during the final decarburization stage the steel is refined by injecting an argon-oxygen mixture. Mechanical and intergranular corrosion tests had positive results.
引用
收藏
页码：32 / 34