Sulphide corrosion cracking of steel and methods of its corrosion protection

被引：0
|
作者：
Nazarov, A.A. [1 ]
机构：
[1] TsNII Konstruktsionnykh Materialov, 'Prometej', Moscow, Russia
来源：
Zashchita Metallov | 1992年 / 04期
关键词：
Steel modifying;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Foreign data are generalized on fracture effect of hydrogen adsorbed by steel corrosion affected by H2S containing environments, on methods used to reveal propensity of steel for sulphide corrosion cracking as well as to protect it. Cracking is prevented through rational choice of steel composition, product design and its operation conditions. As for low alloyed steel of medium strength most rational are deep desulphurization (up to 2×10-3%), alloying with Cu above 3% and control of shape and non-metallic inclusions through modification with calcium at Ca÷S≥2. Chromium-nickel austenitic materials fracture in H2S-chloride mixture at ≥150°.
引用
收藏
页码：531 / 544
相关论文
共 50 条
  • [41] ELECTROCHEMICAL STUDIES OF CELL CORROSION OCCLUSION (CCO) AND PROTECTION AGAINST CORROSION - PITTING CORROSION, CARVENOUS CORROSION, CRACKING CORROSION UNDER PRESSURE, SELECTIVE CORROSION OF ALLOYS - APPLICATION TO IRON AND STEEL, TO COPPER, TO CUPRONICKELS AND TO BRASS
    POURBAIX, M
    VANMUYLDER, J
    VERINK, ED
    POURBAIX, A
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1975, 62 (01): : 219 - 229
  • [42] Test methods and technique of sulfide stress corrosion cracking (SSCC) occurred on steel
    Zhang, Xueyuan
    Du, Yuanlong
    Cailiao Baohu/Materials Protection, 1995, 28 (10): : 18 - 20
  • [43] SIGNIFICANCE OF PROTECTION POTENTIAL IN PITTING, INTERGRANULAR CORROSION AND STRESS-CORROSION CRACKING
    POURBAIX, M
    JOURNAL OF THE LESS-COMMON METALS, 1972, 28 (01): : 51 - &
  • [44] NEW STANDARD SPECIFICATIONS FOR CORROSION AND PROTECTION AGAINST CORROSION OF STEEL
    不详
    STAHL UND EISEN, 1984, 104 (02): : 99 - 102
  • [45] Corrosion Cracking of Kh70 Pipe Steel under the Conditions of Cathodic Protection
    L. I. Nyrkova
    Materials Science, 2020, 56 : 273 - 278
  • [46] Corrosion protection of reinforcing steel with kelp extract as corrosion inhibitor
    Xu, J. X.
    Gao, G. F.
    Jiang, L. H.
    Pang, D. P.
    MATERIALS RESEARCH INNOVATIONS, 2015, 19 : S20 - S25
  • [47] Effects of sulphide on pit corrosion in metallic glass steel
    Shanlin, W.
    Shanben, C.
    Seonghoon, Y.
    Liming, K.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 638 - 641
  • [48] Physico-chemical basis of steel protection against hydrogen sulfide corrosion cracking
    Lyakishev, N.P.
    Alekseev, V.I.
    Efimenko, S.P.
    Bashchenko, A.P.
    Doklady Akademii nauk SSSR, 1995, 341 (02): : 209 - 212
  • [49] Corrosion Cracking of Kh70 Pipe Steel under the Conditions of Cathodic Protection
    Nyrkova, L., I
    MATERIALS SCIENCE, 2020, 56 (02) : 273 - 278
  • [50] STRESS-CORROSION CRACKING OF STEEL WELDMENTS
    FUJII, CT
    METZBOWER, EA
    METALS ENGINEERING QUARTERLY, 1976, 16 (04): : 15 - 20
12345