SUSCEPTIBILITY OF LOW-CARBON Cr-Ni STEEL TO INTERCRYSTALLINE CORROSION.

被引：0

作者：

Savkina, L.Ya.

Lazareva, N.A.

Fel'dgandler, E.G.

Agapova, N.P.

机构：

来源：

Metal Science and Heat Treatment | 1973年 / 15卷 / 1-2期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Steel is not susceptible to ICC with less than 0. 008% C or with Nb/C greater than equivalent to 17. Alloying with around 2% molybdenum and tungsten reduces susceptibility to ICC somewhat. The steel is susceptible to ICC at higher temperatures. The higher the nickel content, the lower the permissible carbon content at which the steel is not susceptible to ICC.

引用

页码：147 / 149

共 50 条

[31] Flow Dependence of the Pitting Corrosion of a Cr-Ni Steel in NaCl Solution - 2.
Herbsleb, G.
Schwenk, W.
Werkstoffe und Korrosion, 1973, 24 (04): : 267 - 268
[32] Corrosion cracking of austenitic Cr-Ni steels and alloys
Kikichev, R.N.
Metally, 2003, (02): : 61 - 66
[33] Structure inheritance and intercrystalline brittleness in high-strength low-carbon alloyed steel
Schastlivtsev, VM
Tabatchikova, TI
Yakovleva, IL
FIZIKA METALLOV I METALLOVEDENIE, 1995, 80 (06): : 96 - 107
[34] Structural inheritance and intercrystalline brittleness in high-strength low-carbon alloy steel
Shchastlivtsev, V.M., 1600, (80):
[35] Effect of Silicon Content on the Susceptibility of Acid-Resistant Austenitic CrNi Steels to Intercrystalline Corrosion.
Cihal, Vladimir
Hutnicke listy, 1980, 35 (10): : 703 - 708
[36] SUSCEPTIBILITY OF LOW-CARBON STEEL TO BRITTLE-FRACTURE
KHRISTENKO, IN
TOMENKO, YS
METAL SCIENCE AND HEAT TREATMENT, 1979, 21 (5-6) : 398 - 399
[37] Susceptibility to Stress Corrosion Cracking for Low-Carbon Steel Welds in Carbonate-Bicarbonate Solution
Mitsui, H.
Takahashi, R.
Asano, H.
Taniguchi, N.
Yui, M.
CORROSION, 2008, 64 (12) : 939 - 948
[38] RESEARCH ON CAUSES OF PITTING CORROSION OF LOW-CARBON STEEL
DEFRANCQ, JN
CORROSION SCIENCE, 1974, 14 (07) : 461 - 465
[39] EFFECT OF CHLORORGANIC ACIDS ON THE CORROSION OF LOW-CARBON STEEL
GOMMA, GK
ELBARADIE, HY
ISSA, RM
SHOKRY, HE
INDIAN JOURNAL OF TECHNOLOGY, 1993, 31 (10): : 725 - 729
[40] HIGH-TEMPERATURE GAS CORROSION OF AUSTENITIC Cr-Ni STEEL CONTAINING Mo AND Ti
Stavrev, D. S.
Dikova, Ts. D.
Ivanov, I. P.
METAL SCIENCE AND HEAT TREATMENT, 2012, 53 (9-10) : 508 - 511

← 1 2 3 4 5 →