SUSCEPTIBILITY OF LOW-CARBON Cr-Ni STEEL TO INTERCRYSTALLINE CORROSION.

被引：0
|
作者：
Savkina, L.Ya.
Lazareva, N.A.
Fel'dgandler, E.G.
Agapova, N.P.
机构：
来源：
Metal Science and Heat Treatment | 1973年 / 15卷 / 1-2期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Steel is not susceptible to ICC with less than 0. 008% C or with Nb/C greater than equivalent to 17. Alloying with around 2% molybdenum and tungsten reduces susceptibility to ICC somewhat. The steel is susceptible to ICC at higher temperatures. The higher the nickel content, the lower the permissible carbon content at which the steel is not susceptible to ICC.
引用
收藏
页码：147 / 149
相关论文
共 50 条
  • [21] Relationship between the corrosion and Cr-Ni content of stainless steel in borax bath
    Junyuan Wang
    Hongfu Wang
    Huachang Wang
    Peng Qu
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26 : 1137 - 1139
  • [22] Relationship between the corrosion and Cr-Ni content of stainless steel in borax bath
    Wang Junyuan
    Wang Hongfu
    Wang Huachang
    Qu Peng
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2011, 26 (06): : 1137 - 1139
  • [23] INTERGRANULAR CORROSION IN STAINLESS CR-NI STEELS
    CIHAL, V
    CORROSION TRAITEMENTS PROTECTION FINITION, 1970, 18 (07): : 441 - &
  • [24] Definition of the stainless steel susceptibility towards intercrystalline corrosion
    Prikhod'ko, V.N.
    Fedorishin, V.V.
    Defektoskopiya, 1992, (11): : 30 - 35
  • [25] CORROSION PATTERN IN CR-NI DENTAL ALLOYS
    GERARDO, C
    FERNANDEZ, MG
    EDELBERG, M
    VIDELA, H
    JOURNAL OF DENTAL RESEARCH, 1986, 65 (04) : 463 - 463
  • [26] CORROSION CRACKING OF LOW-CARBON SPOTLESS STEEL
    LINCHEVSKII, BV
    ROMANOV, VV
    DOKLADY AKADEMII NAUK SSSR, 1959, 129 (05): : 1020 - 1023
  • [27] CORROSION BEHAVIOR OF BORONIZED LOW-CARBON STEEL
    TSIPAS, DN
    NOGUERA, H
    RUS, J
    MATERIALS CHEMISTRY AND PHYSICS, 1987, 18 (03) : 295 - 303
  • [28] Localized corrosion of low-carbon steel at the nanoscale
    Steven C. Hayden
    Claire Chisholm
    Rachael O. Grudt
    Jeffery A. Aguiar
    William M. Mook
    Paul G. Kotula
    Tatiana S. Pilyugina
    Daniel C. Bufford
    Khalid Hattar
    Timothy J. Kucharski
    Ihsan M. Taie
    Michele L. Ostraat
    Katherine L. Jungjohann
    npj Materials Degradation, 3
  • [29] Localized corrosion of low-carbon steel at the nanoscale
    Hayden, Steven C.
    Chisholm, Claire
    Grudt, Rachael O.
    Aguiar, Jeffery A.
    Mook, William M.
    Kotula, Paul G.
    Pilyugina, Tatiana S.
    Bufford, Daniel C.
    Hattar, Khalid
    Kucharski, Timothy J.
    Taie, Ihsan M.
    Ostraat, Michele L.
    Jungjohann, Katherine L.
    NPJ MATERIALS DEGRADATION, 2019, 3 (01)
  • [30] SURFACE TREATMENT OF AUSTENITIC CR-NI STEEL
    YAMAGUCHI, S
    ZEITSCHRIFT FUR METALLKUNDE, 1976, 67 (02): : 135 - 136
12345