FATIGUE CRACK GROWTH RATES IN STRUCTURAL STEELS.

被引：0
|
作者：
Okumura, Toshie
Nishimura, Toshio
Miki, Chitoshi
Hasegawa, Kinji
机构：
来源：
Doboku Gakkai ronbun hokokushu | 1982年 / 322期
关键词：
MATERIALS - Crack Propagation;
D O I：
10.2208/jscej1969.1982.322_175
中图分类号：
TF [冶金工业]; TG14 [金属材料];
学科分类号：
0806 ;
摘要：
Application of the relationship da/dN equals C( DELTA K)**m (da/dN: fatigue crack growth rate, DELTA K: stress intensity factor range, C, m: material constants) is effective in the analysis of fatigue crack growth life. The values of material constants C and m have great influences on the predicted growth life. The values of C and m that determine the upper and lower bounds of the fatigue crack growth rates are calculated in this paper for Japanese structural steels. Furthermore, fatigue crack growth properties of various materials were studied through the analysis of the C and m correlation.
引用
收藏
页码：175 / 178
相关论文
共 50 条
  • [41] Crack initiation and growth path under multiaxial fatigue loading in structural steels
    Reis, L.
    Li, B.
    de Freitas, M.
    INTERNATIONAL JOURNAL OF FATIGUE, 2009, 31 (11-12) : 1660 - 1668
  • [42] Fatigue crack growth under overload/underload in different strength structural steels
    Liang, Hang
    Zhan, Rui
    Wang, Dongpo
    Deng, Caiyan
    Guo, Baichen
    Xu, Xiaohan
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2022, 192
  • [43] Corrosion fatigue crack growth behavior of structural steels in synthetic seawater - considering cavitation bubbles cushing in a fatigue crack
    Hattori, Shuji
    Okada, Tsunenori
    Zairyo/Journal of the Society of Materials Science, Japan, 1988, 37 (418) : 763 - 769
  • [44] Crack growth rates and corrosion fatigue of austenitic stainless steels in high chloride solutions
    Vichytil, C.
    Mori, G.
    Pippan, R.
    Panzenboeck, M.
    Fluch, R.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS X, 2012, 488-489 : 97 - +
  • [45] Fatigue Crack Growth Rates in Pipeline Steels Using Curved M(T) Specimens
    Darcis, Ph. P.
    Treinen, J. M.
    McColskey, J. D.
    JOURNAL OF TESTING AND EVALUATION, 2009, 37 (06) : 511 - 519
  • [46] Fatigue crack growth rates in pipeline steels using curved M(T) specimens
    Materials Reliability Division, NIST, 325 Broadway, Boulder, CO 80305-3328, United States
    J Test Eval, 2009, 6 (511-519):
  • [47] EFFECT OF NEUTRON RADIATION ON FATIGUE CRACK GROWTH-RATES IN STAINLESS-STEELS
    SMITH, HH
    REPORT OF NRL PROGRESS, 1972, (OCT): : 32 - 34
  • [48] NEAR-THRESHOLD FATIGUE CRACK GROWTH-RATES IN STEELS - A SYSTEMATIC ORDERING
    YODER, GR
    COOLEY, LA
    CROOKER, TW
    JOURNAL OF METALS, 1981, 33 (09): : A46 - A46
  • [49] Fatigue crack-initiation from notches in ferritic-pearlitic steels.
    Meziere, Y
    Champavere, R
    Batisse, R
    Mokhdani, C
    Pineau, A
    ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1375 - 1380
  • [50] THRESHOLD CORROSION FATIGUE CRACK GROWTH IN STEELS
    TU, LKL
    SETH, BB
    JOURNAL OF TESTING AND EVALUATION, 1978, 6 (01) : 66 - 74
12345