Reassessment of the Cr-Fe-Ni system

被引：0
|
作者：
机构：
[1] Hillert, Mats
[2] Qiu, Caian
来源：
Hillert, Mats | 1600年 / TMS Titanium Committee, PA, USA卷
关键词：
Chromium Metallography--Phase Diagrams;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The phase diagram and thermodynamic properties of the Cr-Fe-Ni system were reinvestigated using a large amount of experimental information. Ternary parameters for the liquid, α, and γ phases were evaluated, and satisfactory agreement was obtained with experimental data. Several isothermal and vertical sections, as well as various projections, are presented. Comparisons between experimental information and calculated results from different assessments are discussed. It is not possible to get good agreement at the same time for liquidus temperatures and distribution coefficients above 15 wt pct Cr within the present thermodynamic models. The present assessment reproduces the distribution coefficients better than previous assessments.
引用
收藏
相关论文
共 50 条
  • [21] Thermodynamic reassessment of Fe-Cr-Ni system with emphasis on the iron-rich corner
    Miettinen, J
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 1999, 23 (02): : 231 - 248
  • [22] The application of variable theoretical α influence coefficent to the matrix correction in Cr-Fe-Ni stainless steel
    Ying, XH
    Wang, Q
    Cao, GZ
    Yu, MF
    SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24 (12) : 1681 - 1683
  • [23] Selective separation of Cr-Fe-Ni by phosphate precipitation from stainless steel pickling sludge leaching solution
    Shi C.
    Zhang X.
    Yang C.
    Huagong Jinzhan/Chemical Industry and Engineering Progress, 2021, 40 (11): : 6378 - 6384
  • [24] Early stages of discontinuous precipitation reaction in an advanced Cr-Fe-Ni alloy isothermally aged at 800 °C
    Spadotto, J.C.
    Burke, M.G.
    Solórzano, I.G.
    Materials Characterization, 2022, 183
  • [25] Performance evaluation of electro-spark eroded high-volume fraction of Cr-Fe-Ni superalloy
    Raj, Atul
    Misra, Joy Prakash
    Khanduja, Dinesh
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 2022, 236 (15) : 8449 - 8461
  • [26] Assessing the internalization pathways of Cr-Fe-Ni nanoparticles in native Dittrichia viscosa naturally exposed to industrial atmospheric fallout
    Belhaj Abdallah, Bouchra
    Andreu, Irene
    Perez, Viridiana
    Gates, Byron D.
    ENVIRONMENTAL SCIENCE-NANO, 2024, 11 (06) : 2693 - 2702
  • [27] Early stages of discontinuous precipitation reaction in an advanced Cr-Fe-Ni alloy isothermally aged at 800 °C
    Spadotto, J. C.
    Burke, M. G.
    Solorzano, I. G.
    MATERIALS CHARACTERIZATION, 2022, 183
  • [28] SUPERPLASTICITY IN NI-FE-CR SYSTEM
    HAYDEN, HW
    GIBSON, RC
    MERRICK, HF
    BROPHY, JH
    ASM TRANSACTIONS QUARTERLY, 1967, 60 (01): : 3 - &
  • [29] Impacts of local chemical ordering on the primary radiation damage in Cr-Fe-Ni multi-principal element alloys
    Liu, Leqing
    Li, Wenyue
    Wang, Hui
    Wu, Yuan
    Jiang, Suihe
    Zhang, Xiaobin
    Liu, Xiongjun
    Lu, Zhaoping
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2024, 34 (01) : 178 - 186
  • [30] Influence of Al and Ti Alloying and Annealing on the Microstructure and Compressive Properties of Cr-Fe-Ni Multi-Principal Element Alloy
    An, Keyan
    Yang, Tailin
    Feng, Junjie
    Deng, Honglian
    Zhang, Xiang
    Zhao, Zeyu
    Meng, Qingkun
    Qi, Jiqiu
    Wei, Fuxiang
    Sui, Yanwei
    METALS, 2024, 14 (11)
12345