Isolation of carbon and grain boundary carbide effects on the creep and intergranular stress corrosion cracking behavior of Ni-16Cr-9Fe-xC alloys in 360 °C primary water

被引：1
|
作者：
Hertzberg, J.L. [1 ,2 ]
Was, G.S. [3 ]
机构：
[1] Department of Materials Science and Engineering, University of Michigan, United States
[2] Failure Analysis Associates, Menlo Park, CA 94025, United States
[3] Nuclear Engineering Department, University of Michigan, Ann Arbor, MI 48109-2104, United States
来源：
Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science | 1998年 / 29卷 / 13期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：1035 / 1046
相关论文
共 25 条
  • [21] Fractal analysis of Mo and Nb effects on grain boundary character and hot cracking behavior for Ni-Cr-Fe alloys
    Wei, Xiao
    Xu, Mengjia
    Chen, Jingqing
    Yu, Chun
    Chen, Junmei
    Lu, Hao
    Xu, Jijin
    MATERIALS CHARACTERIZATION, 2018, 145 : 65 - 76
  • [22] The effect of grain boundary character distribution on the high temperature deformation behavior of Ni-16Cr-9Fe alloys
    Alexandreanu, B
    Sencer, BH
    Thaveeprungsriporn, V
    Was, GS
    ACTA MATERIALIA, 2003, 51 (13) : 3831 - 3848
  • [23] Oxidation behavior and Stress Corrosion Cracking Susceptibility of Fe27Ni16Cr3.5Al based AFA Alloy in Supercritical Water
    Sun, Shengying
    Zhou, Zhangjian
    Zhang, Lefu
    Tang, Rui
    MATERIALS RESEARCH EXPRESS, 2018, 5 (06):
  • [24] The study of stress application and corrosion cracking on Ni-16 Cr-9 Fe (Alloy 600) C-ring samples by polychromatic X-ray microdiffraction
    Chao, Jing
    Fuller, Marina L. Suominen
    McIntyre, N. Stewart
    Carcea, Anatolie G.
    Newman, Roger C.
    Kunz, Martin
    Tamura, Nobumichi
    ACTA MATERIALIA, 2012, 60 (03) : 781 - 792
  • [25] Comparative studies of the long-term corrosion behavior of Zr-Sn-Fe-Cr-Ni alloys in pure water at 360 °C/18.6 MPa with high and low dissolved oxygen content
    Lei, Aijia
    Dai, Xun
    Du, Yufeng
    Liao, Jingjing
    Deng, Ruiju
    Xu, Jiangtao
    Huang, Xuefei
    JOURNAL OF NUCLEAR MATERIALS, 2025, 603
123